The aim of this study was to assess the strength, durability properties and corrosion resistance of concrete samples using supplementary cementitious blended materials. In this investigation, three supplementary concrete materials (SCMs) were used together with ordinary Portland Cement (OPC) to form cementitious blends at different proportions. The supplementary materials are silica fume (SF), ground granulated blast furnace slag (GGBS) and fly ash (FA). Sixteen (16) different proportions of the cementitious blends were produced. Tests carried out on concrete samples include slump test, compressive strength, oxygen permeability, sorptivity, porosity, chloride conductivity test, resistance to chloride and sulphate attack. The electrode potentials of tested samples were also observed using electrochemical measurements.
Concrete specimens prepared with 10%, 20%, 30%, 40%, up to 60% of blended cements replacement levels were evaluated for their compressive strength at, 7, 14, 28, 90 and 120 days while the specimens were evaluated for durability tests at 28, and 90 days respectively. The results were compared with ordinary Portland cement concrete without blended cement. Voltage, and temperature measurements were also carried out to understand the quality of concrete. The corrosion performance of steel in reinforced concrete was studied and evaluated by electrochemical half-cell potential technique in both sodium chloride, and magnesium sulphate solutions respectively. The reinforced concrete specimens with centrally embedded 12mm steel bar were exposed to chloride and sulphate solutions with the 0.5 M NaCl and MgSO4 concentrations respectively. An impressed voltage technique was carried out to evaluate the corrosion resistance of the combination of quaternary cementitious blended cement, so as to get the combination with optimum performance. Improvement of strength, durability, and corrosion resistance properties of blended concrete samples are observed at different optimum percentages for binary, ternary and quaternary samples. The effect of cementitious blends is recognized in limiting the corrosion potential of the tested SCM concrete samples. Generally, the cementitious blends with limited quantity of SF to 10% have the potential to produce satisfactory concrete. These should however be used for low cost construction, where high quality concrete is not required. / Civil and Chemical Engineering / M. Tech. (Chemical Engineering)
| Identifer | oai:union.ndltd.org:netd.ac.za/oai:union.ndltd.org:unisa/oai:uir.unisa.ac.za:10500/25242 |
| Date | 10 1900 |
| Creators | Akinwale, Abiodun Ebebezer |
| Contributors | Ikotun, B. D. |
| Source Sets | South African National ETD Portal |
| Language | English |
| Detected Language | English |
| Type | Dissertation |
| Format | 1 online resource (xv, 103 leaves) : color illustrations, graphs |
Page generated in 0.0023 seconds