Previous issue date: 2015-08-28 / CAPES / Peças de concreto intertravadas para pavimentação (pavers) coloridas com pigmento de óxido de ferro (vermelho) são utilizadas em projetos de urbanização. Entretanto, esse tipo de pigmento, além de encarecer de 20 a 30% o valor das peças, prejudica as propriedades dos concretos secos moldados sob vibrocompressão. Diante disso, propõe-se incorporar resíduo de cerâmica vermelha (RCV) como matiz colorimétrica em prol da redução de pigmento em pavers coloridos, tendo em vista também a possibilidade de melhoria de suas propriedades por
efeitos filler e pozolânico. A fim de investigar o efeito do pigmento e do RCV no compósito estudado, as formulações foram: (a) traço padrão pelo método de dosagem da ABCP para blocos e pavers; (b) adição de pigmento ao traço padrão (2% e 4%); (c) substituição da areia média pelo RCV no traço padrão (50%, 75% e 100%); (d) adição de RCV ao traço padrão (20%, 30%, 40% e 50%); (e) adição de pigmento (2%) e RCV concomitantemente ao traço padrão (20%, 30%, 40%, 50%, 100% e 150%). Para todos os traços (exceto aqueles das formulações de substituição), foi feita a correção do consumo de cimento em relação ao traço padrão. Resistência à compressão, absorção de água e resistência à abrasão foram avaliadas de acordo com a norma NBR 9781:2013; além disso, foi realizada uma avaliação das cores dos compósitos desenvolvidos por inspeção visual. Pastas de cimento vibroprensadas com baixa relação água-cimento (padrão, 3% pigmento, 15% RCV e 3% pigmento – 15% RCV) também foram moldadas para avaliações de cunho microestrutural, cristalográfico e de análise térmica das reações de hidratação dos sistemas. O traço padrão foi 1:2,29:1,76:0,95 (cimento:areia média:areia muita grossa:pedrisco) com relação água-materiais secos 0,80. De uma maneira geral, adições de apenas pigmento (2% e 4%) reduziram em até 73% a resistência à compressão do paver padrão cinza (sem adições). Redução nos produtos de hidratação (CH e C-S-H) foram observadas. As substituições de areia média pelo RCV também foram prejudiciais a esse sistema. Já as adições de apenas RCV, bem como as de RCV concomitantemente com pigmento foram positivas em ganhos ou manutenção de propriedades (resistência à compressão, absorção de água, resistência à abrasão e cor) em relação ao paver padrão colorido (4% de pigmento), destacando-se a formulação 2% de pigmento e 50% de RCV. Assim, a adição de RCV é uma possibilidade técnica promissora, sustentável e economicamente viável na fabricação de pavers avermelhados. / Concrete interlocking blocks colored with pigment iron oxide (red) are used in urbanization projects. However, that kind of pigment increases around 20 to 30% the value of the pavers, as well as affect the properties of the dry concrete molded by vibrocompression. Therefore, it is proposed to incorporate red ceramic waste (RCW) as colorimetric hue in order of pigment content reduction in colored pavers, considering also the possibility of improving their properties by filler and pozzolanic effect. In order to investigate the effect of pigment and RCW in the studied composite, the formulations were: (a) reference paver designed by ABCP method for blocks and pavers; (B) adding pigment to the reference paver (2% and 4%); (C) substitution of medium sand by RCW in the reference paver (50%, 75% and 100%); (D) adding RCW in the reference paver (20%, 30%, 40% and 50%); (E) addition of pigment (2%) and RCW concurrently in the reference paver (20%, 30%, 40%, 50%, 100% and 150%). For all mixtures (except those of replacement formulations), it was made the correction in cement consumption related to the reference mix proportion. Compressive strength, water absorption and abrasion resistance were measured according to the ABNT NBR 9781: 2013 standards; besides that, the color and texture of all manufactured formulations were observed by visual inspection. Cement pastes made by vibrocompression with low water-cement ratio (reference paste, 3% pigment, 15% RCW and 3% pigment RCW - 15% RCW) were also molded for microstructural, crystallographic and thermal analysis of systems hydration reactions. The reference mix proportion was 1:2.29:1.76:0.95 (cement: medium sand: thick sand: gravel) with ratio water-dry material 0.80. In general, additions of only pigment (2% and 4%) up to 73% reduced the compressive strength of the reference paver (no additions). Reduction in hydration products (C-S-H and CH) was observed. The substitution formulations of medium sand by RCW were also harmful to the systems. Additions of only RCW and RCW concomitantly with pigment were positive in gains or maintaining of properties (compressive strength, water absorption resistance and abrasion resistance) compared to the reference colored paver (4% pigment), especially the formulation of 2% pigment and 50% RCW. Thus, the addition of RCW is a promising, economic and sustainable technique in the production of red pavers.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpe.br:123456789/16647 |
| Date | 28 August 2015 |
| Creators | ALCANTARA, Paloma Santos Xavier de |
| Contributors | NÓBREGA, Ana Cecília Vieira da |
| Publisher | Universidade Federal de Pernambuco, Programa de Pos Graduacao em Engenharia Civil e Ambiental, UFPE, Brasil |
| Source Sets | IBICT Brazilian ETDs |
| Language | Breton |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFPE, instname:Universidade Federal de Pernambuco, instacron:UFPE |
| Rights | Attribution-NonCommercial-NoDerivs 3.0 Brazil, http://creativecommons.org/licenses/by-nc-nd/3.0/br/, info:eu-repo/semantics/openAccess |
Page generated in 0.0032 seconds