The present study investigates the fracture toughness of FSW X-80 HSLA steel welds. Weld cooling rate and peak temperature were varied among welds; indirectly manipulated through FSW travel speed, rpm, and weld preheat. Fracture toughness was tested according to ASTM 1820 standard along the weld centerline using surface-notched SEB specimen cooled to -40 °C. This study resulted in a reliable, repeatable process for generating friction stir welds with CTOD’s consistently above that of the original base metal. CTOD and microstructure of friction stir welds can be selected by controlling weld cooling rate and peak temperature. Material properties and microstructure similar to the original base metal can be recreated throughout the weld stir zone. CTOD of FSW X80 has a strong inverse linear correlation with post-weld cooling rate.
| Identifer | oai:union.ndltd.org:BGMYU2/oai:scholarsarchive.byu.edu:etd-10171 |
| Date | 27 July 2021 |
| Creators | Crook, Nolan Tracy |
| Publisher | BYU ScholarsArchive |
| Source Sets | Brigham Young University |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | Theses and Dissertations |
| Rights | https://lib.byu.edu/about/copyright/ |
Page generated in 0.0019 seconds