The present diploma thesis concerns the research of plasmachemical reduction of copper corrosion layers. The process was based on using low pressure hydrogen RF plasma in which copper samples are treated for several hours. Four series of copper corrosion layers were prepared in four different corrosion atmospheres. The first two were prepared using saturated vapors of HCl and ammonium acetate that affected copper samples for one week. The second two sets were prepared by samples dipping in HNO3 and H2SO4. EDX analysis confirms visual composition of corrosion layers – chlorides, nitrides and sulphate, respectively. The ammonium acetate produced no corrosion layers and thus this set of samples was omitted. The optical emission spectroscopy was used to find out reactions in a hydrogen RF discharge. At the first, a character of plasma without samples was taken by measuring in continuous and pulsed regime. The integral spectrum intensity (300-700 nm) and intensities of hydrogen atomic lines were observed in the dependences on hydrogen flow, power and duty cycle. After that copper samples were treaded under various conditions in continual and pulse regime, typically at pressure of 170 Pa, 200 W power and hydrogen flow rate of 10.2 ml/min. The integral OH radical spectral intensity in the range of 305 – 330 nm was used as a monitor of plasma treatment process. The experimental results showed that intensities of OH radical depended strongly on the corrosion layer kind as well as on the RF discharge mode. Reduction of corrosion layers treated in the pulsed regime was not so satisfactory then in the continuous regime probably due to lower temperature of sample during the treatment. The total supplied energy into the system was also lower in this case. The sample sputtering was observed during the reduction in continuous regime. It means the corrosion was successfully removed but the process was not stopped at that moment, so it is necessary to propose another additional monitoring process besides observing OH radicals. Our experimental results are the first step in the spread research of plasmachemical treatment of copper made archaeological artifacts.
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:216405 |
Date | January 2008 |
Creators | Šimšová, Tereza |
Contributors | Selucká, Alena, Krčma, František |
Publisher | Vysoké učení technické v Brně. Fakulta chemická |
Source Sets | Czech ETDs |
Language | Czech |
Detected Language | English |
Type | info:eu-repo/semantics/masterThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0017 seconds