Ruthenium, proposed as a new candidate of diffusion barrier, has three different kinds of oxides, which are native oxide, electrochemical reversible oxide and electrochemical irreversible oxide. Native oxide was formed by naturally exposed to air. Electrochemical reversible oxide was formed at lower anodic potential region, and irreversible oxides were formed at higher anodic potential region. In this study, we were focusing on the effect of copper electrodeposition on each type of oxides. From decreased charge of anodic stripping peaks and underpotential deposition (UPD) waves in cyclic voltammetry (CV), efficiency of Cu deposition dropped off indicating that interfacial binding strength between Cu and Ru oxides was weakened when the Ru surface was covered with irreversible oxide and native oxide. Also, Cu UPD was hindered by both O2 and H2 plasma modified Ru surfaces because the binding strength between Cu and Ru was weakened by O2 and H2 plasma treatment. Cu/Ru and Cu/Ta bimetallic corrosion was studied for understanding the corrosion behavior between diffusion barrier (Ta and Ru) and Cu interconnects under the post chemical mechanical planarization (CMP) process in semiconductor fabrication. Gallic acid is used in post CMP slurry solution and is known well as antioxidant which is supposed to oxidize itself to prevent other species from oxidizing. However, in this study under the observation of Cu microdot corrosion test, copper was corroded only in gallic acid at specific pH region of alkaline condition which is close to the pH region for post CMP solution formula. With different pH alkaline condition, gallic acid formed different oxidized products which are characterized by cyclic voltammetry and UV-Vis spectroscopy. Therefore, the specific oxidized product from particular pH region condition caused the Cu corrosion. Also, the corrosion rate of Cu microdots was influenced by substrate effect (Cu/Ru and Cu/Ta) and ambient control, which was included in this study.
Identifer | oai:union.ndltd.org:unt.edu/info:ark/67531/metadc3897 |
Date | 08 1900 |
Creators | Yu, Kyle K. |
Contributors | Chyan, Oliver M. R., Golden, Teresa D. |
Publisher | University of North Texas |
Source Sets | University of North Texas |
Language | English |
Detected Language | English |
Type | Thesis or Dissertation |
Format | Text |
Rights | Public, Copyright, Yu, Kyle K., Copyright is held by the author, unless otherwise noted. All rights reserved. |
Page generated in 0.0261 seconds