In this work, the possibility of Cu electrodeposition on Ru-Ta alloy thin films is explored. Ru and Ta were sputter deposited on Si substrate with different composition verified by RBS. Four point probe, XRD, TEM and AFM were used to study the properties of Ru-Ta thin films such as sheet resistance, crystallinity, grain size, etc. Cyclic voltammetry is used to study the Cu electrodeposition characteristics on Ru-Ta after various surface pretreatments. The results provide insights on the removal of Ta oxide such that it enables better Cu nucleation and adhesion. Bimetallic corrosion of Cu on modified Ru-Ta surface was studied in CMP related chemicals. In Cu interconnect fabrication process, the making of trenches and vias on low-k dielectric films involves the application of fluorocarbon plasma etch gases. Cu microdots deposited on Ru and Ta substrate were treated by fluorocarbon plasma etch gases such as CF4, CF4+O2, CH2F2, C4F8 and SF6 and investigated by using x-ray photoelectron spectroscopy, contact angle measurement and electrochemical techniques. Micropattern corrosion screening technique was used to measure the corrosion rate of plasma treated Cu. XPS results revealed different surface chemistry on Cu after treating with plasma etching. The fluorine/carbon ratio of the etching gases results in different extent of fluorocarbon polymer residues and affects the cleaning efficiency and Cu corrosion trends.
| Identifer | oai:union.ndltd.org:unt.edu/info:ark/67531/metadc84286 |
| Date | 08 1900 |
| Creators | Sundararaju Meenakshiah Pillai, Karthikeyan |
| Contributors | Chyan, Oliver Ming-Ren, Richmond, Michael G., Verbeck, Guido F., Youngblood, W. Justin |
| Publisher | University of North Texas |
| Source Sets | University of North Texas |
| Language | English |
| Detected Language | English |
| Type | Thesis or Dissertation |
| Format | Text |
| Rights | Public, Sundararaju Meenakshiah Pillai, Karthikeyan, Copyright, Copyright is held by the author, unless otherwise noted. All rights reserved. |
Page generated in 0.002 seconds