The diploma thesis deals with influence of fast pressure-less sintering on the microstructure of advanced ceramic materials, namely -Al2O3 and tetragonal ZrO2 (doped by 3 mol% Y2O3) with particle sizes ranging from 60 nm to 270 nm. Fast and controlled heating rate was enabled by utilization of the special superkanthal furnace with moving sample holder. Defect-free bulk and dense samples were prepared using heating rates in order of 100-200 °C/min. Higher densities reached the samples pressed by higher pressures; the specimens with densities higher than 99 % t.d. were prepared within tens of minutes for alumina as well as for zirconia with very low thermal conductivity. Different behavior was observed only for material TZ-3Y, which exhibited core-shell structure with dense surface and porous centre after sintering at heating rates higher than 10 °C/min. It was shown in this work that such behavior was not primarily caused by the high thermal gradient resulting from high heating rates. Its creation was probably caused by chlorine impurities. The mechanism of desintering of these samples was described and eliminated by calcination of the samples at 1000 °C for 10 hours prior to fast sintering at 1500 °C, so even this material could be fast sintered up to 99.9 % theoretical density.
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:319861 |
Date | January 2017 |
Creators | Prajzler, Vladimír |
Contributors | Chlup, Zdeněk, Maca, Karel |
Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
Source Sets | Czech ETDs |
Language | Czech |
Detected Language | English |
Type | info:eu-repo/semantics/masterThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0015 seconds