Inhibitors used as dopant anions in polymer films are responsible for the anticorrosion behaviour of polypyrrole (Ppy). Ppy film doped with MoO42- and TiF62- showed the role of anions in corrosion protection of iron. Ppy doped with 3-nitro salicylate was used for zinc protection. The results of XPS revealed that molybdate exist in two types: [MoO4]2- (62%) and [Mo7O24]6- (28%). Electrochemical Impedance Spectroscopy (EIS) has indicated the change of the resistance RPM and the capacitance CPM of the Ppy film during reduction. Electrochemical Quartz Crystal Microbalance (EQCM) has shown: the mass of the Ppy film decreased in the cathodic region and increased in the anodic region. The anion flux was also observed in Scanning Kelvinprobe (SKP) and X-ray Photoelectron Spectroscopy (XPS) experiments. The release behaviour of molybdate anions depends much on the size of cations in the electrolyte. TiF62- anions has shown good inhibitor properties. However, the mechanism of this action is not yet known. 3-nitro salicylate (3-nisa) was used as inhibitor dopant for zinc in this work. Ppy film could be formed on Zn without any special pretreatment. The dissolution of Zn decreased dramatically in the presence of 3-nisa. The application of Ppy/metal inorganic composites in corrosion protection for mild steel and galvanised steel may be a better selection. Mixture of core-shell particles with matrix polymer was used as primer for protective coatings.
| Identifer | oai:union.ndltd.org:DRESDEN/oai:qucosa.de:swb:14-1128413485169-50124 |
| Date | 04 September 2005 |
| Creators | Minh Duc, Le |
| Contributors | Technische Universität Dresden, Mathematik und Naturwissenschaften, Chemie, Institut für Physikalische Chemie und Elektrochemie, Prof. Dr. W. Plieth, Prof. Dr. J. Heitbaum, Prof. Dr. H.-J. Adler, Prof. Dr. W. Plieth |
| Publisher | Saechsische Landesbibliothek- Staats- und Universitaetsbibliothek Dresden |
| Source Sets | Hochschulschriftenserver (HSSS) der SLUB Dresden |
| Language | English |
| Detected Language | English |
| Type | doc-type:doctoralThesis |
| Format | application/pdf |
Page generated in 0.0025 seconds