Resistência à corrosão de ligas Ni-Cr-Mo em meios fluoretados para aplicações odontológicas

Made available in DSpace on 2014-06-11T19:32:50Z (GMT). No. of bitstreams: 0
Previous issue date: 2011-12-01Bitstream added on 2014-06-13T21:05:02Z : No. of bitstreams: 1
silva_jwj_dr_guara.pdf: 2585287 bytes, checksum: b0304efc039af53412ee1f7353c6f71a (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Um grande número de ligas metálicas é usado na Odontologia para fabricação de próteses fixas e removíveis. Na cavidade oral essas estruturas estão expostas a um meio quimicamente adverso, com a saliva sendo o agente mais corrosivo, devido à alta concentração de íons cloreto que são causadores de corrosão localizada. Além disso, soluções contendo íons fluoreto também são frequentemente utilizadas em agentes profiláticos nos tratamentos dentários para prevenir a formação de placas dentárias e o desenvolvimento de cáries. Neste sentido, considerou-se importante investigar o comportamento eletroquímico e a resistência à corrosão de ligas dentárias Ni-Cr-Mo em meio fluoretado tamponado, que simula a agressividade dos colutórios e dos cremes dentários. Para tanto, foram realizados ensaios eletroquímicos de corrosão, em uma solução tampão HF/NaF, de três ligas avaliadas comercialmente (N, W 99 e SB) que se diferenciam com respeito às mudanças nas suas composições químicas, em especial, nos teores de níquel e de cromo. Para maior compreensão da morfologia das ligas estudadas, foi realizada a análise metalográfica, utilizando-se microscopia óptica e microscopia eletrônica de varredura. Para avaliar o comportamento eletroquímico, foram aplicadas técnicas eletroquímicas tradicionalmente utilizadas nas pesquisas de corrosão, tais como: polarização potenciodinâmica (PDS), polarização cíclica (CP) e espectroscopia de impedância eletroquímica (EIS). De acordo com os resultados obtidos, verificou-se o melhor desempenho para a liga N e o pior para W99, apresentando SB um comportamento intermediário. / A great number of metal alloys is used in dentistry to manufacture fixed and removable prostheses. In oral cavity these structures are exposed to a chemically adverse environment, with saliva being the most corrosive agent, due to high chloride ions concentration, which are causing localized corrosion. Moreover, solutions containing fluoride ions are also commonly used in prophylactic agents in dental treatments to prevent dental plaque formation and caries expansion. Thus, it was considered important to investigate the electrochemical behavior and corrosion resistance of Ni-Cr-Mo dental alloys in buffered fluoride medium, which simulates aggressiveness of mouthwashes and dental creams. This being so, electrochemical corrosion tests were carried out in a buffer HF/NaF solution of three commercially evaluated alloys (N, W 99 and SB) which are different in relation to changes in chemical compositions, in particular, in nickel and chromium content. For a better understanding of the studied alloys morphology, it was performed metallographic analysis, by using optical microscopy and scanning electron microscopy. In order to evaluate the electrochemical behavior, it was applied electrochemical techniques traditionally used in corrosion research, such as: potentiodynamic polarization (PDS), cyclic polarization (CP) and electrochemical impedance spectroscopy (EIS). According to the obtained results, it was observed the best performance for N alloy and the worst for W 99, with SB presenting and intermediate behavior.

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/103759
Date01 December 2011
CreatorsSilva, José Wilson de Jesus [UNESP]
ContributorsUniversidade Estadual Paulista (UNESP), Codaro, Eduardo Norberto [UNESP], Nakazato, Roberto Zenhei [UNESP]
PublisherUniversidade Estadual Paulista (UNESP)
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis
Format129 f. : il.
SourceAleph, reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP
Rightsinfo:eu-repo/semantics/openAccess
Relation-1, -1, -1

Page generated in 0.002 seconds