Orientador: Carlos Kenichi Suzuki / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-07-26T14:59:54Z (GMT). No. of bitstreams: 1
Iano_MarcosChogi_M.pdf: 12731426 bytes, checksum: 662fae0d81de8813d1edefc6157fe126 (MD5)
Previous issue date: 2000 / Resumo: A avançada indústria da informação utiliza em larga escala o quartzo sintético na forma de dispositivos eletrônicos como ressonadores, filtros de ondas, osciladores, dispositivos SA W (Surface Acoustic Waves), polarizadores entre outros, que exigem alta qualidade cristalina da matéria-prima. Desta forma, o avanço desta área está ligado ao aprimoramento e desenvolvimento das propriedades do quartzo sintético, que por sua vez está intimamente relacionado as sementes. O objetivo deste projeto é obter através do emprego de geometrias especiais de corte das sementes o aprimoramento do cristais de quartzo sintético de alta perfeição cristalina visando: (i) a diminuição ou mesmo, a eliminação dos defeitos do tipo linhas de discordâncias; (ü) a reconstituição de regiões da semente contendo defeitos do tipo geminado elétrico ("Dauphiné twin"). E neste contexto, aplicar o processo de crescimento rápido na direção X, o que poderá abrir novas perspectivas para a obtenção de sementes de grandes dimensões a partir do quartzo natural. Além do aspecto tecnológico, existe um forte interesse sócio-econômico para o país, uma vez que o Brasil possui a maior reserva mundial de quartzo natural com qualidade e dimensões compatíveis para este fim, que são exportados sem nenhum processo de agregação de tecnologia e valor. Para o desenvolvimento deste estudo foi utilizado uma interface de colaboração científica com a empresa Fine Crystal Co., do Japão que realizou o crescimento hidrotérmico de cristais sintéticos a partir de sementes preparadas no Laboratório Ciclo Integrado do Quartzo, Unicamp/FEM. Neste caso, foram utilizadas barras de quartzo caracterizadas e com especificações bem definidas, por exemplo, com concentração de discordâncias de 400, 100 e 30 linhas/cm 2. Para caracterização e análise dos cristais crescidos hidrotermicamente utilizou-se a técnica de topografia por difração de raios-X, que mostrou um aprimoramento efetivo na eliminação de linhas de discordâncias e no re-crescimento de regiões com defeitos / Abstract: The advanced industry of information technology has been utilizing a large amount of synthetic quartz for electronic devices, such as resonators, wave filters, oscillators, SA W (Surface Acoustic Waves) devices. One important condition for these applications is the high perfection of synthetic quartzo Therefore, the progress of this area is closely related with the development of synthetic quartz properties, and consequently, with seed technology for growing perfect and large crystals. The aim of this research is to obtain through the employment of special geometry cuttings of seed, an improvement of synthetic quartz crystals, in terms of: (i) decreasing or eliminating dislocation lines; (ii) the reconstitution or re-growing seed regions with Dauphiné twins. In this context, the application of fast growth in + X direction will open new perspectives to obtain seeds of great dimensions from natural quartzo Besides the technological aspect, there is a strong social and economical interest for this country, due to the fact that the largest and the best quartz reserve of piezoelectric grade big blocks are situated in Brazil. This strategic quartz resource has been exported in natura with no processing. For the development of this research, a scientific collaboration was conducted between the Laboratory of Integrated Quartz Cyc1e (LIQC), Faculty of Mechanical Engineering, UNICAMP, and Fine Crystal Co., Japan, where the synthetic quartz was hydrothermally grown. The used seed in this experiment was totally prepared in LIQC, using a series of know-how we have developed during the last fifieen years. Very well characterized quartz bars containing 400, 100, and 30 dislocation lines/cm2 where used for the seed preparation. X-ray diffiaction topography used for the characterization of as-grown synthetic quartz crystals shows that the elimination of dislocation lines, and the re-growing of imperfect regions (after cutting out) were very effective / Mestrado / Materiais e Processos de Fabricação / Mestre em Engenharia Mecânica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/264930 |
| Date | 02 November 2000 |
| Creators | Iano, Marcos Chogi |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Suzuki, Carlos Kenichi, 1945-, Yoshimura, Junichi, Arruda, Antonio Celso |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 100p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0019 seconds