RPE do ion Fe3+ em monocristais e fibras de LiNbO3 / ERP of Fe3+ ion in single crystals and fibres of LiNbO3

O objetivo deste trabalho foi o estudo do íon Fe3+ em monocristais e fibras monocristalinas de LiNbO3, através da técnica espectroscópica da Ressonância Paramagnética Eletrônica (RPE), nas freqüências de 10 e 34GHz, à temperatura ambiente. O Hamiltoniano de Spin para o íon Fe3+ ocupando um sítio de simetria trigonal (C3v) é dado por: H = \'beta\' \'VET.H\' \'VET.g\' \'VET.S\' + \'B20O20+B40O40 . Foram analisadas três amostras de LiNbO3, com diferentes concentrações de Fe3+ e os parâmetros de campo cristalino e fator-g encontrados são: fibra (0.3 mol% de Fe3+) g = 1.9908 \'+OU-\' 0.0002, \'B. SUP. 0 INF. 2\' = 5.4\'+OU-\'0.2x10-2 cm-1 , \'B. SUP. 0 INF. 4\' = -7.7\'+OU-\'1.5x10-5cm-1, monocristal 90 (0.22 mol%) g = 2.0043\'+OU-\'0.0002, \'B. SUP. 0 INF. 2\' = 5.35\'+OU-\'0.25x10-2 cm-1, \'B. SUP. 0 INF. 4\'= - 4.03\'+OU-\'1.4x10-5cm-1, monocristal 99 (0.02 mol%) g = 2.0026\'+OU-\'0.0004, \'B. SUP. 0 INF. 2\' = 5.4\'+OU-\'0.3x10-2 cm-1, \'B. SUP. 0 INF. 4\' = - 8.33\'+OU-\'1.6x10-5cm-1. Foi medida e analisada a dependência angular da largura das linhas nas duas bandas de freqüências. Através de modelos teóricos (Watanabe, Orbach-Das-Sharma, Spinspin, Spin-spin Spin-órbita) calculamos o parâmetro de desdobramento a campo zero, \'B. SUP. 0 INF. 2\', do estado fundamental do íon Fe3+, para determinar qual o sítio que este íon ocupa no LiNbO3. / We report EPR measurements of Fe3+ ion in bulk LiNbO3 single crystals and in the form of fibers. Spin Hamiltonian for the Fe3+ ion in a trigonal symmetry (C3v) site is given by: H = \'beta\' \'VET.H\' \'VET.g\' \'VET.S\' + \'B20O20+B40O40. Measurements were performed at room temperature and two frequency bands, 10 and 34GHz, using three samples of LiNbO3 with different concentrations of Fe3+ g-factor and the crystal field parameters were found to be: for fiber (0.3 mol% of Fe3+) g = 1.9908 \'+OU-\' 0.0002, \'B. SUP. 0 INF. 2\' = 5.4\'+OU-\'0.2x10-2 cm-1 , \'B. SUP. 0 INF. 4\' = -7.7\'+OU-\'1.5x10-5cm-1, for the single crystal 90 (0.22 mol%) g = 2.0043\'+OU-\'0.0002, \'B. SUP. 0 INF. 2\' = 5.35\'+OU \'0.25x10-2 cm-1, \'B. SUP. 0 INF. 4\'= - 4.03\'+OU-\'1.4x10-5 cm-1, and for the single crystal 99 (0.02 mol%) g = 2.0026\'+OU-\'0.0004, \'B. SUP. 0 INF. 2\' = 5.4\'+OU-\'0.3x10-2 cm-1, \'B. SUP. 0 INF. 4\' = - 8.33\'+OU-\'1.6x10-5cm-1. The angular dependence of the line width were also measured and compared with theoretical model. To determine the substitutional site of Fe3+ ion in the LiNbO3 lattice, we calculated the zero field splitting parameter \'B. SUP. 0 INF. 2\' of the ground state, using many theoretical models (Watanabe, Orbach-Das-Sharma, Spin-spin, Spin-Spin Spinorbita).

Identiferoai:union.ndltd.org:IBICT/oai:teses.usp.br:tde-09042008-084147
Date19 August 1994
CreatorsRicardo Costa de Santana
ContributorsMaria Cristina Terrile, Claudio Jose Magon, Valmor Roberto Mastelaro
PublisherUniversidade de São Paulo, Física, USP, BR
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Sourcereponame:Biblioteca Digital de Teses e Dissertações da USP, instname:Universidade de São Paulo, instacron:USP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.002 seconds