Superplasticidade de um aço inoxidavel duplex

Orientadores: Ana M. M. Nazar, Ricardo E. Medrano / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-07-22T01:43:55Z (GMT). No. of bitstreams: 1
Sagradi_DeboraPulino_D.pdf: 12577810 bytes, checksum: a9c00a427e30de3148040672fc53ed66 (MD5)
Previous issue date: 1996 / Resumo: Não informado / Abstract: Superplasticity is the ability of certain materials to deform homogeneously with high elongations (several hundreds or thousands percent) at elevated temperatures and low strain rates. This subject of scientific and teclinological interest is not well slablished yet. The purpose of present work is to characterize and to study the superplastic behavior of a 22.5%Cr-6.4%Ni-3.0%Mo-0.16%N duplex stainless steel. Therefore, samples from sheets of the material were examined at 950°C and 98CFC by means of tensile, strain rate change and stress relaxation tests. Moreover, microstructures and cavitation process under main conditions were also analyzed. Tensile tests provided informations about elongation and deformation homogeneity. On the other hand, the strain rate change and stress relaxation tests were more suitable to determine the strain rate sensitivity. The superplastic behavior analysis was based on whole results from elongation, strain rate sensitivity and deformation uniformity. According to these criteria, the material exhibits superplastic deformation at 980X with strain rates ranging from 10 s" to ! 0' s". Under these conditions the deformation was homogeneous (without necking), the strain rate sensitivity coefficient attained 0.7 and elongation achieved 900%. During deformation: (i) the initial microstructure composed of oriented phases change to an equiaxed stable structure and (ii) cavitation process occurs. These observations suggest the grain boundary sliding as the main superplastic deformation mechanism. Key Words: super-plasticity, duplex stainless steel, tensile test, strain rate change test, stress relaxation / Doutorado / Materiais e Processos de Fabricação / Doutor em Engenharia Mecânica

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/263048
Date18 November 1996
CreatorsSagradi, Debora Pulino
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, Martinez Nazar, Ana Maria, 1948-, Medrano, Ricardo Enrique, 1937-, Nazar, Ana Maria Martinez, Ferreira, Itamar, Ammann, Jean-Jacques, Isore, Alain Jean, Falleiros, Ivan Gilberto Sandoval
Publisher[s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis
Format163f. : il., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0026 seconds