Orientador: Marcelo Giannini / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-27T08:07:39Z (GMT). No. of bitstreams: 1
Ruivo_MelissaAraujo_M.pdf: 7058282 bytes, checksum: ccb6c2382e6c36e7f4a50d09e21434b8 (MD5)
Previous issue date: 2015 / Resumo: O plasma tem sido utilizado em diversas áreas da Odontologia como no clareamento dental, pois produz espécies reativas que contribuem para o clareamento através da clivagem das cadeias orgânicas dos agentes cromógenos e através da sua capacidade em aumentar a energia de superfície. Os objetivos desse estudo foram avaliar a ação do plasma associado ao peróxido de hidrogênio na alteração de cor, concentração de cálcio e fósforo e rugosidade de superfície do esmalte, utilizando as análises de espectrofotometria de reflectância, espectroscopia dispersiva por raio-X (EDX) e microscopia confocal. Foram utilizadas as porções coronárias vestibulares de dentes bovinos, os quais foram manchados com solução de chá preto e posteriormente divididos em cinco grupos: grupo PH3 (3 aplicações de peróxido de hidrogênio 38% por 15 minutos), grupo PL1+PH1 (1 aplicação de plasma por 1 minuto + 1 aplicação de peróxido de hidrogênio 38%), grupo PL1+PH3 (3 aplicações de plasma por 1 minuto + 3 aplicações de peróxido de hidrogênio 38%), grupo PL2+PH1 (1 aplicação de plasma por 2 minutos + 1 aplicação de peróxido de hidrogênio 38%), grupo PL2+PH3 (3 aplicações de plasma por 2 minutos + 3 aplicações de peróxido de hidrogênio 38%). Os dentes foram submetidos a duas sessões de clareamento, e na parte do estudo sobre a alteração de cor, as análises foram feitas após cada sessão de clareamento. Nas análises de EDX e rugosidade, a leitura foi feita apenas após a segunda sessão de clareamento. Além disso, para as análises de EDX e rugosidade foi introduzido um grupo controle que não recebeu o tratamento clareador, nem o plasma. Foram realizadas quatro tomadas de cores (análise dos parâmetros "L*", "a*", "b*" e "?E"): inicial (sem tratamento), após o manchamento e após a primeira e segunda sessões de clareamento. Os dados dos parâmetros "L*" e "b*" foram analisados por meio de análise de variância (ANOVA 2 fatores) e teste de Tukey¿Kramer (?=0,05) e para o parâmetro "a*", foram realizados testes não-paramétricos (Kruskal Wallis, Dunn e Friedman). Para a análise da concentração de cálcio e fósforo e rugosidade de superfície, os dados foram submetidos à análise de variância (1 fator) e teste de Tukey (5%). Os grupos PH3, PL1+PH3 e PL2+PH3 não diferiram entre si na análise de "b*" e "?E". Nas avaliação de "L*", "a*" e "b*" houve diferença significativa após a segunda sessão de clareamento em todos os grupos. Apenas o grupo PH3 apresentou redução da concentração de cálcio e fósforo comparado ao grupo controle (sem clareamento) e todos os grupos tratados com clareamento apresentaram aumento da rugosidade em relação ao grupo controle na análise da rugosidade (remover). Os grupos que receberam os maiores tempos de aplicação de plasma e peróxido de hidrogênio (PL1+PH3 e PL2+PH3) tenderam produzir melhores efeitos clareadores, comparados aos grupos que receberam apenas uma aplicação, como pode ser observado nas análises do parâmetro "b*" e do ?E. O uso do plasma manteve a concentração de cálcio e fósforo. Todos os grupos que envolveram clareamento, com ou sem aplicação do plasma, promoveram aumento da rugosidade de superfície do esmalte / Abstract: Plasma has been used in several areas of Dentistry even for tooth whitening, because produces reactive species that contribute to tooth whitening by cleavage of the organic chains of chromogens and the increasing of energy surface. The aims of this study were to evaluate the effect of hydrogen peroxide combined with argon plasma on color change, calcium and phosphorus concentration, surface roughness and enamel surface morphology, using reflectance spectrophotometry analysis, dispersive X-ray spectroscopy (EDX) and confocal microscopy. Vestibular coronal portions of bovine teeth were used, which were stained with black tea solution and then divided into five groups: Group PH3 (3 applications of 38% hydrogen peroxide for 15 minutes), PL1+PH1 group (1 plasma application of 1 minute + one application of 38% hydrogen peroxide), PL1+PH3 group (3 plasma applications of 1 minute + three application of 38% hydrogen peroxide), PL2+PH1 group (1 plasma application of 2 minutes + one application of 38% hydrogen peroxide), PL2+PH3 group (3 plasma applications of 2 minutes + three application of 38% hydrogen peroxide). For color measurements were performed (parameter "L*", "a*", "b*" and "?E"): initial (untreated), after staining and after bleaching (first and second sessions). For chemical composition and roughness analysis, samples were only analyzed before treatment (control group) and after two bleaching sessions. Data of "L*" and "b*" color parameters were analyzed by analysis of variance (two-way ANOVA) and Tukey-Kramer test (?= 0.05), while nonparametric tests (Kruskal Wallis, Dunn e Friedman) for the parameter "a*". The concentrations of calcium and phosphorus data was analyzed by one-way ANOVA (5%). PH3, PL1+PH3 and PL2+PH3 groups did not differ for "b" and "?E" analysis. For "L*", "a*" and "b*" parameters, there was a significant difference after second bleaching session for all groups regarding the stained teeth. Only PH3 group decreased the concentration of calcium and phosphorus compared to untreated control group and all bleached groups differed significantly from control group, regarding the surface roughness. Groups that received more amount of argon plasma and hydrogen peroxide (PL1+PH3 and PL2+PH3) tended to enhance the whitening compared to the groups with only one application of hydrogen peroxide, as observed in the analysis of the parameters "b*" and ?E. The use of plasma preserves the concentration of calcium and phosphorus elements. All bleached groups, with plasma application or not promoted increasing of enamel surface roughness / Mestrado / Materiais Dentarios / Mestra em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/287803 |
| Date | 27 August 2018 |
| Creators | Ruivo, Melissa Araújo, 1990- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Giannini, Marcelo, 1969-, Sundfeld, Renato Herman, Lima, Débora Alves Nunes Leite |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 79 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0029 seconds