Orientador: Debora Alves Nunes Leite Lima / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-27T07:56:52Z (GMT). No. of bitstreams: 1
Gouveia_ThaylaHellenNunes_M.pdf: 2628593 bytes, checksum: 44232982dae72b94fe8955775a8a2ab8 (MD5)
Previous issue date: 2015 / Resumo: O objetivo deste estudo in vitro foi avaliar as propriedades físicas de uma resina composta nanoparticulada submetida ao envelhecimento artificial acelerado (AAA), ação de agentes clareadores e manchamento extrínseco. O estudo foi dividido em 2 experimentos. O experimento 1 avaliou a influência do AAA e do peróxido de carbamida a 16% com diferentes espessantes na retenção do brilho (GU), cor (?E), microdureza (KHN) e rugosidade média (Ra) de superfície do compósito. A análise qualitativa da superfície de resina foi realizada através de microscopia de força atômica. Cem amostras cilíndricas (7,0mm x 2,0mm) foram confeccionadas e distribuídas aleatoriamente em 10 grupos (n=10). Somente metade dos grupos foram envelhecidos. Para o tratamento clareador/espessante, os grupos com e sem AAA foram divididos em: peróxido de carbamida 16% (PC) com carbopol, PC com natrosol, gel de carbopol, gel de natrosol e sem tratamento (controle). Os dados obtidos foram analisados por meio de ANOVA dois fatores e teste de Tukey. Para o ?E as comparações múltiplas foram realizadas pelos teste de Tukey e Dunnett. Os valores de rugosidade foram analisados pelos testes de Kruskal Wallis, Dunn e Mann Whitney. O nível de significância considerado foi de 5%. O PC com carbopol promoveu redução apenas na microdureza do compósito, diferindo estatisticamente do controle. Para o PC com natrosol esta alteração não foi observada. O PC com carbopol aumentou a rugosidade e diminuiu o brilho das resinas envelhecidas, enquanto o natrosol só o briho foi reduzido, diferindo estatisticamente do grupo controle. O Experimento 2 avaliou a influência dos tratamentos clareadores em diferentes concentrações e manchamento com café na propriedades físicas anteriormente citadas da resina nanoparticulada, submetidas ou não ao AAA. Duas amostras representativas de cada grupo foram avaliadas em microscopia eletrônica de varredura. Cento e vinte amostras cilíndricas foram confeccionadas, semelhante ao estudo anterior, distribuídas em 12 grupos (n=10). Metade das amostras foram envelhecidas artificialmente. Para o tratamento clareador/pigmentação, os grupos com e sem AAA, foram divididos em: peróxido de carbamida a 10% (PC 10%), peróxido de hidrogênio a 35% (PH 35%) e sem tratamento clareador, com e sem pigmentação por café. Os dados foram coletados e submetidos a ANOVA três fatores e teste de Tukey para comparações múltiplas. Para o ?E as comparações múltiplas foram realizadas pelos testes de Tukey e Dunnett (?=0,05). Nas resinas sem envelhecimento, os agentes clareadores reduziram a microdureza do compósito, entretanto a rugosidade, brilho e cor não apresentaram alterações. Após o envelhecimento, o PC 10% aumentou a rugosidade e diminuiu o brilho comparado ao PH 35%. A pigmentação também reduziu a microdureza das resinas sem e com envelhecimento e alterou a cor das resinas envelhecidas (?E>25). Portanto, a ação dos géis clareadores reduziu a microdureza do nanocompósito, sendo que a composição do gel clareador influenciou nessa alteração. O AAA promoveu significativas alterações nas propriedades físicas avaliadas, além de favorecer uma maior degradação da superfície da resina pelo agente clareador e este efeito contribuiu para um maior manchamento extrínseco / Abstract: The aim of this in vitro study was to evaluate the physical properties of a nanocomposite subjected to artificial accelerated aging (AAA), to the action of bleaching agents and to extrinsic staining. This study was divided into two experiments. Experiment 1: evaluate the influence on a composite surface of AAA and 16% carbamide peroxide with different thickeners, in gloss retention (GU), color (?E), microhardness (KHN) and roughness (Ra). Qualitative analysis of the resin surface was performed by atomic force microscopy. One hundred cylindrical samples (7.0mm x 2.0mm) were prepared and randomly divided into 10 groups (n = 10). Only half of the groups were aged. For the bleaching/thickening treatment, the groups with and without AAA were divided into groups/ treatments: 16% carbamide peroxide (PC) with carbopol, PC natrosol, carbopol gel, natrosol gel and untreated (control). Data were submitted to two-way ANOVA and Tukey¿s test for multiple comparisons. The multiple comparisons for ?E were performed by using Tukey¿s and Dunnett¿s tests, and roughness values was analysed by using Kruskal-Wallis, Dunn¿s, and Mann-Whitney¿s tests (? =0.05). The PC with carbopol promoted a decreased in the composite microhardness differing significantly from the control. As for CP + natrosol this change in the microhardness was not observed. The treatment with CP + carbopol increased the roughness and decreased the gloss of the aged resins, whereas natrosol reduced only the gloss which differed statistically from the control. Experiment 2: evaluate the influence of bleaching treatments with different concentrations and coffee staining, in the physical properties of nanocomposite, submitted or not to AAA. Two representative samples of each group were evaluated in scanning electron microscopy (SEM). One hundred twenty cylindrical samples were prepared similar to the previous study and divided into 12 groups (n = 10). Half of specimens were artificially aged. For the bleaching/pigment treatment, groups with and without AAA, were divided into the following groups: 10% carbamide peroxide (10% CP), 35% hydrogen peroxide (35% PH) without bleaching treatment, with and without pigmentation of coffee. Data were submitted to three-way ANOVA and Tukey¿s test for multiple comparisons. The multiple comparisons for ?E were performed by using Tukey¿s and Dunnett¿s tests (?=0,05). The resins without aging, the bleaching agents promoted a reduction in the composite microhardness, however, in the roughness, gloss and color this changes were not observed. After aging, the pigmentation also reduced the microhardness of the resins with and without aging and altered the color of the aged resins (?E> 25). 10% PC increased roughness and decreased gloss compared to 35% PH. Pigmentation also reduced the microhardness of the resins with and without aging and change the color of the aging resins (?E> 25). The action of bleaching agents reduced the microhardness of the nanocomposite, and this alteration was influenced by the composition of the bleaching gel. The AAA promoted significant changes in the evaluated physical properties and favored the further deterioration of the resin surface by the bleaching, contributing to a greater extrinsic staining / Mestrado / Dentística / Mestra em Clínica Odontológica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/290657 |
| Date | 27 August 2018 |
| Creators | Gouveia, Thayla Hellen Nunes, 1985- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Lima, Débora Alves Nunes Leite, 1978-, Santos, Maria do Carmo Moreira da Silva, Paulillo, Luis Alexandre Maffei Sartini |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
| Source Sets | IBICT Brazilian ETDs |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 73 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0052 seconds