The dispersion of graphene in 1,2-dichloroethane (DCE), its subsequent attachment at the water-DCE interface and the reduction of oxygen at the water-DCE interface proceeding via interfacial graphene have been investigated. Using addition of an electrolyte which screens surface charge, it was found that electrostatic repulsions play a significant role in determining the kinetic stability of lyophobic non-aqueous graphene dispersions. The onset of aggregation was determined and it was found that dispersions prepared from higher-oxygen content graphite were more stable than those prepared from lower-oxygen content graphite, indicating that oxygen content is important in determining the surface charge on graphene in non-aqueous dispersion. The presence of organic electrolyte was also found to promote assembly of graphene into a coherent film at the liquid-liquid interface. Measurement of the liquid-liquid interfacial tension and three-phase contact angle revealed that the energetics of particle attachment did not change in the presence of organic electrolyte, thus indicating a mechanism of inter-particle electrostatic repulsion minimisation through surface charge screening. Interfacial graphene was found to display a catalytic effect toward the oxygen reduction reaction at the water-DCE interface. A bipolar cell was developed which showed that this reaction occurs heterogeneously, with graphene acting as a conduit for electrons across the water-DCE interface.
| Identifer | oai:union.ndltd.org:bl.uk/oai:ethos.bl.uk:674697 |
| Date | January 2015 |
| Creators | Rodgers, Andrew Norman John |
| Publisher | University of Manchester |
| Source Sets | Ethos UK |
| Detected Language | English |
| Type | Electronic Thesis or Dissertation |
| Source | https://www.research.manchester.ac.uk/portal/en/theses/dispersion-assembly-and-electrochemistry-of-graphene-at-the-liquidliquid-interface(c2ffd27a-cf5f-45c2-a471-60dcab788e12).html |
Page generated in 0.002 seconds