The master’s thesis is focused on the application of the technique of oriented foils in transmission electron microscopy. Dislocation structures were identified by this technique in both phases of polycrystalline austenitic-ferritic stainless steel SAF 2507 formed during low cycle fatigue at two plastic strain amplitudes ap. In individual grains the stress axis and the Schmid factors of active slip systems were determined. In austenitic grains, the planar structures were determined at both ap. In ferritic grains, the dislocation arrangement was different for the two observed ap. Individual screw dislocations and pile-up´s of edge dislocations were found at low ap = 1x10-4. Mixture of vein and wall dislocation structures were formed at high ap = 2x10-3. Observed dislocation structures were discussed in relation with the cyclic plastic response of the duplex stainless steel.
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:228855 |
Date | January 2009 |
Creators | Buček, Petr |
Contributors | Kruml, Tomáš, Petrenec, Martin |
Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
Source Sets | Czech ETDs |
Language | Czech |
Detected Language | English |
Type | info:eu-repo/semantics/masterThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0013 seconds