CoordenaÃÃo de AperfeiÃoamento de Pessoal de NÃvel Superior / In the last years, the fractal geometry has become widely studied. Its application in several areas increased substantially, particularly in materials engineering and science, aiming the analysis of failures and the study of the mechanical properties of materials. Some studies have shown the relationship between the fracture surfaces and their mechanical properties using the fractal geometry and its properties of fractal dimension and selfsimilarity.
In this research, the fracture surface of duplex stainless steel, which was obtained by the Charpy impact test, was studied applying the fractal geometry. Considering the 475ÂC embrittlement, the steel was submitted to thermal aging to obtain the fracture surfaces, whose images were captured by the scanning electron microscope (SEM). In the fractal analysis, a study was made applying the island method and profile analysis through the digitalization of the images and the application of image analyzing software.
Emphasis was given on the calculation of the fractal dimension (FD) of the surface, on the energy absorbed during the impact test, on the involved fracture mechanisms and as well on the relationship between FD and thermal aging. In order to better understanding the subject, it was done the review about fracture mechanics, of duplex stainless steel and of fractal geometry. Finishing the research, the obtained fracture surface, the absorbed energy and the obtained values of FD were analyzed. The
obtained results demonstrated a relationship between the fractal dimension, the size of the dimples in fracture surfaces and the impact energy to obtain them. / A geometria dos fractais nos Ãltimos anos tem se tornado bastante difundida no meio cientÃfico. O seu emprego em diversas Ãreas aumentou substancialmente, em particular na engenharia e ciÃncia dos materiais, com o objetivo de analisar falhas e estudar as propriedades mecÃnicas dos materiais. Alguns estudos tÃm mostrado a relaÃÃo entre as propriedades mecÃnicas de superfÃcies de fratura com a geometria dos fractais e suas propriedades de dimensÃo fractal e auto-similaridade.
Nesta pesquisa, foi estudada, com base na geometria dos fractais, a superfÃcie de fratura do aÃo inoxidÃvel duplex obtida atravÃs do ensaio de impacto Charpy. Considerando a fragilizaÃÃo a 475C, o aÃo foi submetido ao tratamento tÃrmico de envelhecimento para a obtenÃÃo das superfÃcies de fraturas cujas imagens foram captadas no microscÃpio eletrÃnico de varredura (MEV). Na anÃlise fractal foi feito um estudo aplicando os mÃtodos das ilhas e anÃlise de perfil atravÃs da digitalizaÃÃo das imagens e aplicaÃÃo de softwares de anÃlise de imagem. Foi dada Ãnfase na anÃlise do cÃlculo da dimensÃo fractal (Df) da superfÃcie, na energia absorvida no ensaio de impacto, nos mecanismos de fratura envolvidos, bem como na relaÃÃo entre Df e o tratamento tÃrmico de envelhecimento. Para o melhor entendimento do trabalho foi feita uma revisÃo bibliogrÃfica sobre a mecÃnica da fratura, o aÃo inoxidÃvel duplex e a geometria dos fractais. Para finalizar a pesquisa, foi feita a anÃlise da superfÃcie da fratura obtida, da energia absorvia e de valores de Df alcanÃados. Os resultados obtidos demonstraram uma relaÃÃo entre a dimensÃo fractal, o tamanho dos dimples em superfÃcies de fratura e a energia de impacto para a obtenÃÃo das mesmas.
| Identifer | oai:union.ndltd.org:IBICT/oai:www.teses.ufc.br:5236 |
| Date | 18 October 2002 |
| Creators | Eloy de Macedo Silva |
| Contributors | Ãnio Pontes de Deus, Telmo Roberto Strohaecker, Josà Mauricio Oliveira Matos |
| Publisher | Universidade Federal do CearÃ, Programa de PÃs-GraduaÃÃo em Engenharia e CiÃncia de Materiais, UFC, BR |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | application/pdf |
| Source | reponame:Biblioteca Digital de Teses e Dissertações da UFC, instname:Universidade Federal do Ceará, instacron:UFC |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0013 seconds