Previous issue date: 2010 / Resumo: É apresentada a preparação e a caracterização de nanocompósitos, produzidos a partir da vermiculita e poliolefinas funcionalizadas como matriz polimérica. As poliolefinas foram representadas pelo polietileno de baixa densidade (PEBD) e o polietileno de baixa densidade linear (PEBDL), utilizadas com e sem o anidrido maleico. A vermiculita de origem nacional foi escolhida como fase inorgânica na preparação dos nanocompósitos, devido a sua abundância e o seu baixo custo associado. A interação das matrizes poliolefínicas com a vermiculita foi facilitada pela utilização de agentes de acoplamento, baseados em compostos de amônio, cujos efeitos sobre as propriedades de barreira, ao oxigênio, à umidade, e de retardância de chama dos compostos obtidos são relatados. Foi utilizada como ferramenta de análise a Espectroscopia de Infravermelho com transformada de Fourier (FTIR), para o acompanhamento e caracterização do processo de síntese das organo-vermiculitas. A Difração de Raio X (DRX) foi utilizada tanto para a análise do minério de vermiculita como recebido, quanto para a caracterização dos nanocompósitos utilizando as vermiculitas modificadas com os agentes de acoplamento. Os resultados foram confirmados com a utilização da Microscopia Eletrônica de Transmissão (MET) e a Microscopia Eletrônica de Varredura (MEV), com auxílio da técnica de feixe de íons (FIB). Essas técnicas confirmaram a obtenção de compostos esfoliados, evidenciando a eficiência dos agentes de acoplamento no processo de obtenção dos nanocompósitos, previamente analisados via DRX. A estrutura esfoliada dos compostos obtidos permitiu que fossem conduzidos testes sobre a sua capacidade de barreira ao oxigênio e a umidade, cujos resultados promissores mostraram a possibilidade de serem utilizados como materiais de embalagem. Da mesma forma, a característica esfoliada destes materiais possibilitou o desenvolvimento de testes para o atendimento da área de fios e cabos como isolamento e cobertura de cabos. Com este objetivo, foram analisados os requisitos de retardância de chama e ao aumento da temperatura de degradação, fundamental à preservação da integridade dos cabos durante o ataque das chamas. Este trabalho apresentou de maneira pioneira o processo de produção e utilização da vermiculita nacional, na obtenção de nanocompósitos, desde minério bruto até o produto final e a sua aplicação em casos reais / Abstract: The preparation and characterization of nanocomposites made from vermiculite and functionalized polyolefins as a polymeric matrix is presented. Polyolefins are represented by low-density polyethylene (LDPE) and linear low-density polyethylene (LLDPE), used with and without maleic anhydride. Vermiculite from a national origin was chosen as an inorganic phase in the nanocomposite preparation, due to its abundance and low cost. The interaction of the polyolefin matrixes with the vermiculite was facilitated using coupling agents. The coupling agents used were represented by the ammonium compounds and their effects were reported in the barrier properties to oxygen, humidity and in flame retardance in the produced compounds. As a nanocomposite analysis tool, Fourrier transformed infrared spectroscopy (FTIR) techniques were used, mainly in following and characterizing the organo-vermiculite process. X-ray diffraction (XRD) was used from the analysis of the vermiculite as received to the nanocomposite characterization using coupling agents. These results were confirmed using the transmission electronic microscopy (TEM) and scanning electronic microscopy (SEM), using focused ion beam (FIB), as well. These techniques confirmed the obtainment of exfoliated compounds that reinforced the coupling agents in the nanocomposite obtainment process, previously analyzed by XRD. The exfolied structure of the compounds obtained allowed for barrier-capacity tests. The nanocomposites tested as an oxygen and humidity barrier showed the possibility of being used as packaging materials due to the promising results presented. Likewise, the exfoliated characteristic of these materials enabled the development of tests to meet the needs of the wire and cable area as insulation and cable jacketing. Within this objective, there was the need to focus on the flame retardance requirements and the increase of the degradation temperature, crucial to preserve cable integrity during the flame attack. This work presents, in a pioneering manner, a revision of the production process and utilization of national vermiculite in obtaining the nanocomposite, from its ore to the final product and its application in real cases / Doutorado / Ciencia e Tecnologia de Materiais / Doutor em Engenharia Química
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/266883 |
| Date | 16 August 2018 |
| Creators | Carvalho, José Wilson Camilher |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Mei, Lúcia Helena Innocentini, 1953-, Scuracchio, Carlos Henrique, Segala, Karen, Bagnato, Osmar, Ravagnani, Sergio Persio |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Química, Programa de Pós-Graduação em Engenharia Química |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 107 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0031 seconds