Developing novel tanning agents from renewable biomass is regarded as an effective strategy for sustainable leather industry. In this study, a series of dialdehyde carboxymethyl cellulose (DCMC) were
prepared by periodate oxidation of carboxymethyl cellulose (CMC) with varying degrees of substitution (DS: 0.7, 0.9 and 1.2). The structural properties of DCMC were characterized. Size Exclusive
Chromatography measurements showed that CMC underwent severe degradation during periodate oxidation, resulting in the decline of weight-average molecular weight from 250,000 g/mol to around
13,000 g/mol. FT-IR analysis illustrated that aldehyde group was successfully introduced into DCMC. The aldehyde group content of DCMC decreased from 8.38 mmol/g to 2.95 mmol/g as the DS rose from 0.7 to 1.2. Interestingly, formaldehyde was found to be produced in DCMC, and its content was 159.4, 151.7 and 38.4 mg/L, respectively when the DS of CMC was 0.7, 0.9 and 1.2, respectively. Further analysis by HPLC found that fructose was formed during oxidative degradation, and was subsequently oxidized to generate formaldehyde. This was in accordance with the fact that higher DS resulted in lower formaldehyde content in DCMC. The whole reaction mechanism is still under investigation at the moment. Tanning trials showed that the shrinkage temperature and thickening rate of DCMC tanned leather decreased as the DS increased. This should be due to the difference in aldehyde content of DCMC. Leather tanned by DCMC-0.7 (DS of CMC was 0.7) had the highest shrinkage temperature of 81°C and thickening rate of 76%. It was noteworthy that the formaldehyde content in DCMC tanned leather was only 0.11-0.40 mg/kg even though DCMC contained a small amount of formaldehyde. In general, we hope the work on dialdehyde tanning agent derived from CMC could provide some essential data for the development of sustainable tanning material and process.
Take-Away:
1. Higher degree of substitution (DS) of CMC resulted in lower aldehyde group content of DCMC.
2. The formaldehyde content of DCMC was negatively correlated with DS.
3. The tanning performance of DCMC with lower DS was better.
| Identifer | oai:union.ndltd.org:DRESDEN/oai:qucosa:de:qucosa:34165 |
| Date | 26 June 2019 |
| Creators | Yi, Yudan, Ding, Wei, Jiang, Zhicheng, Wang, Ya-nan, Bi |
| Contributors | International Union of Leather Technologists and Chemists Societies |
| Publisher | Verein für Gerberei-Chemie und -Technik e. V., Forschungsinstitut für Leder und Kunststoffbahnen (FILK) gGmbH |
| Source Sets | Hochschulschriftenserver (HSSS) der SLUB Dresden |
| Language | English |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, doc-type:conferenceObject, info:eu-repo/semantics/conferenceObject, doc-type:Text |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | urn:nbn:de:bsz:14-qucosa2-340872, qucosa:34087 |
Page generated in 0.0022 seconds