Orientadores: Rubens Caram Junior, Adelino Aguiar Coelho / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-08-08T17:54:45Z (GMT). No. of bitstreams: 1
Andrade_ProtasioNery_M.pdf: 9178937 bytes, checksum: f63ed0f47d8aa70b2d3a755e537fbe8f (MD5)
Previous issue date: 2006 / Resumo: Em função de características como alta razão resistência/peso, ótima biocompatibilidade, elevada resistência à corrosão e módulo de elasticidade que pode ser controlado pela adição de elementos de liga, o uso de ligas de titânio pela indústria médica e odontológica está em franco crescimento. No presente estudo, ligas do sistema Ti-Cu com teores entre 5 e 15 % em peso de cobre foram fundidas através do processo de fundição por centrifugação em moldes de cobre. A alta taxa de resfriamento imposta pelo molde empregado levou à formação de microestruturas totalmente martensítica. Em seguida, tais microestruturas foram modificadas através tratamentos térmicos, levando a estruturas mais estáveis. A caracterização das amostras obtidas envolveu análise microestrutural através de microscopia óptica e eletrônica de varredura, difração de raios-X, ensaios mecânicos. Os resultados obtidos indicam que as altas taxas de resfriamento envolvidas promoveram a formação da estrutura metaestável _'. O aumento da concentração de cobre levou ao aumento na dureza promovida pela formação do intermetálico Ti2Cu. O Ti2Cu apresentou módulo de elasticidade menor do que a fase _. A fratura dos corpos de prova teve caráter dúctil e é intensamente afetada pela presença de porosidade / Abstract: Due to characteristics like high strength-to-weight ratio, high biocompatibility, enhanced corrosion resistance and the possibility of controlling elastic behavior by proper addition of alloying elements, the use of titanium by medical and dental industries is continuously growing. In this work, Ti-Cu alloys with a Cu content varying from 5% to 15 wt% were prepared by arc melting and cast in copper molds. The high cooling rate imposed by copper mold led to the formation of a completely martensitic structure. Following, the microstructure of these samples were modified by applying proper heat treatments, leading to more stable microstructures. The samples characterization includes microstructure analyzes through optical and scanning electron microscopy, X-ray diffraction method and mechanical tests. The results obtained suggest that application of high cooling rates resulted in the formation of a'metastable phase. As Cu content was increased, hardness also increased due to Ti2Cu intermetallic compound precipitation. The Ti2Cu compound was found to present lower elastic modulus than the modulus of a phase. Finally, it was found that the heat treated samples presented high ductility and their mechanical behavior is affected by porosities / Mestrado / Materiais e Processos de Fabricação / Mestre em Engenharia Mecânica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/263193 |
| Date | 28 July 2006 |
| Creators | Andrade, Protasio Nery |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Coelho, Adelino de Aguiar, Caram Junior, Rubens, 1958-, Junior, Rubens Caram, Robert, Maria Helena, Ierardi, Maria Clara Filippini |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0028 seconds