Orientadores: Lourenço Correr Sobrinho, Simonides Consani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-18T20:46:54Z (GMT). No. of bitstreams: 1
CarrilhoNeto_Antonio_D.pdf: 8464064 bytes, checksum: 16996840d4c6ac4cececfc832c5f7e73 (MD5)
Previous issue date: 2011 / Resumo: O objetivo neste estudo foi avaliar a influência de sistemas de polimento e escovação mecânica simulada, sobre o brilho, rugosidade e integridade da superfície de materiais restauradores estéticos. Quatro compósitos foram avaliados: Filtek Z350 XT - 3M ESPE, Charisma Opal - Heraeus Kulzer, Amelogen Plus - Ultradent, Tetric N-Ceram - Ivocler Vivadent. Vinte amostras cilíndricas padronizadas foram obtidas para cada material e separadas aleatoriamente em 2 grupos (n=10), sendo que cada grupo foi submetido a um dos dois procedimentos de polimento (Sof-Lex - 3M ESPE e PoGo - Dentsply Caulk). Em seguida, todas as amostras foram submetidas às avaliações de brilho, mensurado com medidor (Zehntner ZGM 1120 Glossmeter) e a rugosidade com rugosímetro (Surfcorder SE1700 - Kosaka Lab) e submetidas a 30000 ciclos mecânicos de escovação simulada, utilizando solução de dentifrício (Colgate) e água destilada. Na seqüência da escovação, as mensurações de brilho e rugosidade foram repetidas. Em seguida, as amostras foram submetidas aos procedimentos de polimento, seguidos das avaliações de brilho e rugosidade. Os dados foram submetidos à ANOVA para medidas repetidas e teste de Tukey (p?0,05). Adicionalmente, amostras iniciais, escovadas e polidas foram examinadas em microscopia eletrônica de varredura (5600LV - Jeol) para avaliação qualitativa da integridade da superfície. Com base nos resultados de Rugosidade Média encontrados após a escovação simulada, pode-se concluir que a resina nanoparticulada apresentou menor rugosidade pela escovação mecânica (0,275 ?m) e maior brilho por ambos os métodos de polimento (PoGo 71,78 GU e Sof-Lex 70,64 GU); A escovação mecânica aumentou os valores médios de rugosidade e diminuiu o brilho dos compósitos; Os sistemas de polimento não foram capazes de recuperar a lisura quando comparados à fase inicial; Ambos os sistemas de polimento melhoraram o brilho deixado pela escovação, com exceção do compósito Amelogem Plus. Com base nas análises das imagens do MEV, foi possível observar que o sistema de polimento de múltiplos passos (Sof-Lex - 3M ESPE) favorece a presença de sulcos profundos / Abstract: The purpose in this study was to evaluate the influence of polishing systems and simulated mechanical toothbrushing, about gloss, rugosity and integrity on surfaces of esthetic restorative materials. Four composites were evaluated: Filtek Z350 Supreme (tem que colocar "supreme" no ingles?) XT (3M ESPE), Charisma Opal (Heraeus Kulzer), Amelogen Plus (Ultradent) and Tetric NCeram (Ivoclair Vivadent). Twenty cylindrical standardized specimens, for each material, were fabricated and ramdomly divided in two groups (n=10), each group being submitted to one of the two polishing protocols (Sof-Lex - 3M ESPE; POGO Dentsply Caulk). After, all specimens were submitted to the following evaluations, surface optical gloss was determined using a glossmeter (ZGM 1120 Glossmeter - Zehntner) and surface roughness was measured with a surface profilometer ( Surfcorder SE 1700 -Kosaka Lab.), and specimens were submitted to 30,000 mechanical simulated brushing cycles, with a dentifrice-water slurry (Colgate) and distilled water. Following brushing, gloss and roughness measurements were evaluated again. Then, specimens were submitted to the polishing process, followed by gloss and roughness evaluations. Data were submitted to ANOVA statistical analysis for repeated measures and Tukey Test (p?0,05). Additionally, initial specimens, brushed and polished, were evaluated under scanning electron microscopy (5600 LV-Jeol) for qualitative surface integrity. Based on the middle rugosity results found after simulated brushing, could be concluded that nanometric composites showed lower rugosity when submitted to mechanical simulated toothbrushing (0,275 ?m) and higher gloss with both polishing protocols (PoGo 71,78 GU e Sof-Lex 70,64 GU); mechanical tooth brushing increased the rugosity middle values and decreased the composite gloss; The polishing systems were not capable to recover smoothness when compared to the initial phase (polyester matrix); both polishing system improved gloss given by brushing, exceptionally for the Amelogen Plus composite. Based on MEV image analysis, was observed that the multiple step polishing system (Sof-Lex - 3M ESPE) favors the presence o deep sulcus / Doutorado / Materiais Dentarios / Doutor em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289607 |
| Date | 18 August 2018 |
| Creators | Carrilho Neto, Antonio, 1962- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Consani, Simonides, 1939-, Correr Sobrinho, Lourenço, 1960-, Contreras, Edwin Fernando Ruiz, Guiraldo, Ricardo Danil, Paula, Andreia Bolzan de, Mesquita, Marcelo Ferraz |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 69 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0028 seconds