Orientador: Regina Maria Puppin Rontani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-10-05T18:49:21Z (GMT). No. of bitstreams: 1
Correr_AnaRosaCosta_D.pdf: 3218831 bytes, checksum: f30505368b581fed81781723b234fbd9 (MD5)
Previous issue date: 2013 / Resumo: O propósito deste estudo foi avaliar a influencia de diferentes tipos de substrato (Capitulo 1) e tratamento com etanol 100% (Capitulo 2) ou digluconato de clorexidina a 2% (CHX) (Capitulo 3) na resistência e longevidade da união compósito/dentina, apos diferentes períodos de armazenagem. Os dentes humanos hígidos foram divididos em 3 grupos, de acordo com o substrato dentinario: (Sd) dentina hígida, (Ci) dentina infectada (manutenção da carie) e (Ca) dentina afetada (remoção parcial de carie). As superfícies oclusais de terceiros molares hígidos foram removidas com disco diamantado dupla face sob refrigeração, a fim de expor a superfície plana dentinaria hígida, a qual foi submetida ao desenvolvimento da lesão de carie artificial com S. mutans. Brocas esféricas foram usadas para remover parcialmente o tecido cariado pigmentado, ate que permanecesse apenas a dentina levemente corada (Ca). Em seguida, os dentes foram novamente subdivididos, de acordo com o tratamento da superfície: Grupo Controle (Ct) - nenhum tratamento (Capitulo 1); Ct e (Et) - aplicação de etanol 100% (Capitulo 2); e, Ct e (CHX) - aplicação de digluconato de clorexidina a 2% (Capitulo 3). O substrato foi condicionado com acido fosfórico a 35% por 15 s, lavado por 30 s e seco com leve jato de ar. CHX ou Et foram aplicados apos o condicionamento acido. O sistema adesivo Adper Single Bond 2 (3M ESPE) foi aplicado de acordo com as recomendações do fabricante e fotoativado por 20 s com a fonte de aparelho de luz XL 2500. Sobre a superfície de união foram inseridos incrementos de 2 mm do compósito Z350 (3M ESPE), polimerizados usando a fonte de luz XL 2500 por 40 s, ate confeccionar um bloco com 6 mm de altura. As amostras foram armazenadas em água destilada a 37o C por 24 horas. Apos, os dentes foram seccionados perpendicularmente a área de união, de modo a obter palitos com área de secção transversal de 1mm2. Os palitos foram armazenadas em três períodos: 24 horas, 6 meses e 1 ano. Em seguida, as amostras foram submetidas ao ensaio de resistência de união a microtração usando a maquina de ensaio EZ test (EZS, Shimadzu) a velocidade de 0,5 mm/minuto. Os dados foram submetidos a Analise de Variância e ao teste de Tukey HSD (?=0,05). A união em Sd mostrou valores de resistência de união significativamente maior quando comparado a Ca e Ci. As amostras armazenadas nos períodos de 6 meses e 1 ano resultou na diminuição da resistência de união, independente do tipo de substrato e/ou tratamento. O etanol não foi efetivo em melhorar a resistência de união para os três substratos de dentina avaliados. A clorexidina não influenciou na resistência de união nos períodos de armazenagem avaliados, independente dos substratos / Abstract: The aim of this study was to evaluate the effect of 2% chlorhexidine digluconate (CHX) and 100% ethanol wet-bonding (Et) on the degradation of the adhesive system bond strength in sound or artificial caries-affected/infected dentin after different storage times under microtensile test (_TBS). The sound teeth were divided into 3 groups, according to dentin substrates: sound dentin, caries-infected dentin (maintained of caries) and caries-affected dentin (partial removal of caries). Non-carious human third molars had their occlusal enamel removed with a slow speed diamond saw, under copious water-cooling to expose a flat-surfaced sound dentin, which was submitted to the microbiological challenge (S. mutans) for the development of artificial caries. Spherical drill was used to remove soft pigmented carious tissue till hard and slightly pigmented dentin remains (Ca). After, the teeth will be assigned into 3 subgroups according to surface treatment: water wet- bonding (Ct) (Chapter 1); Ct and 100% ethanol application (Et) (Chapter 2); and, Ct and chlorhexidine digluconate 2% application (CHX) (Chapter 3). The substrate will was etched with 35% phosphoric acid gel for 15 s, rinsed for 30 s with tap water and dried with oil/water-free air. The CHX or Et was applied for 60 s, just after etching with 35% phosphoric acid gel. The adhesive system Adper Single Bond 2 (3M ESPE) was applied according to the manufacturer's instruction and polymerized for 10 s by a light-curing unit XL 2500. The bonded surfaces were coupled with a composite resin Filtek Z350 (3M ESPE) applied in 2 mm increments and polymerized using a curing unit XL 2500 (3M ESPE) for 40 s for each increment and to build 6 mm thick block. The restored teeth were stored in distilled water at 37o C for 24 h. After this period, the restored teeth were longitudinally sectioned across the bonded interface to produce a series of 1.0mm2 beams. The specimens were then submitted to three storage periods: 24 hours, 6 months, or 1 year. Afterwards, the storage periods, the specimens were submitted to a microtensile bond strength (_TBS) using EZ test machine (EZS, Shimadzu) at a crosshead speed of 0.5 mm/min until failure. Data were submitted to ANOVA and Tukey's HSD test (?=0.05). The bonding with sound dentin showed _TBS values significant higher when compared to caries-affected and caries-infected dentin. The 6 months and 1 year storage periods resulted in decreased bond strengths for all dentin conditions and/or treatment. The ethanol was not effective to improve the _TBS for the three dentin substrates evaluated. The CHX did not affect the 24- hour, 6 and 12 months _TBS, independent of the tested dentin substrates / Doutorado / Materiais Dentarios / Doutora em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288584 |
| Date | 05 October 2018 |
| Creators | Costa, Ana Rosa, 1977- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Puppin-Rontani, Regina Maria, 1959-, Borges, Gilberto Antonio, Neto, Manoel Damião de Sousa, Consani, Simonides, Soares, Carlos José |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 97 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.002 seconds