O objetivo deste trabalho foi analisar em Microscopia Ótica (MO), Espectroscopia micro-Raman (µR) e Microscopia Eletrônica de Varredura (MEV), a interface adesiva em dentina proporcionada por três sistemas adesivos aplicados in vivo e in vitro. Na condição in vivo, pacientes com primeiros prémolares superiores hígidos indicados para extração, por razões ortodônticas, foram utilizados. Cavidades classe I com 0,5mm além da junção esmalte-dentina foram realizadas, nos dentes, com broca carbide 245 em alta rotação. Foram, então aplicados três sistemas adesivos diferentes foram aplicados, de acordo com as instruções dos respectivos fabricantes: Single Bond (SB-3M), Clearfil SE Bond (CSEB-Kuraray) e One Up Bond-F (OUB-Tokuyama). Aplicados esses, as cavidades foram restauradas incrementalmente com resina composta TPH Spectrum (Dentsply). Em seguida os dentes foram extraídos e armazenados em solução de timol a 0,1%. In Vitro, os mesmos procedimentos foram realizados em pré-molares extraídos. Após os dentes foram levados à uma máquina de cortes e seccionados, com auxílio de um disco de corte em espécimes contendo a interface, com dimensões 2mmx2mmx6mm de comprimento, sendo 2 espécimes para cada dente. Um dos espécimes foi levado a um micrótomo de tecido duro onde fatias com espessura de 5µm foram obtidas e coradas com Tricromo de Goldner. As fatias foram, então, analisadas em um microscópio óptico com aumento de 100 vezes. Nesta técnica a dentina mineralizada se cora de verde, o colágeno não infiltrado de vermelho e o sistema adesivo de beje translúcido. Após o mesmo espécime foi utilizado para análise em espectroscopia micro-Raman. O espécime adjacente foi desidratado em seqüência ascendente de etanol e analisado em microscopia eletrônica de varredura. Os resultados da MO para o sistema SB mostraram a presença de uma grande área corada de vermelho, indicando colágeno exposto ou não devidamente infiltrado pelo sistema adesivo para ambas as situações porém, in vivo, esta camada se mostrou maior. Para o sistema CSEB esta camada se corou de roxa, consistente ao longo de toda interface, indicando também a presença de colágeno disponível para reação com o corante, para ambas as situações. Para o sistema OUB esta camada também se corou de roxa, porém in vivo esta se mostrou mais fina e irregular que in vitro. Em MEV o sistema SB apresentou uma camada híbrida granular e porosa para ambas as situações. In vitro esta se mostrou mais espessa e regular ao longo da interface ao contrário da condição in vivo. Grandes diferenças foram observadas em relação aos tags de resina, onde in vivo, se apresentaram mais finos e curtos. Para o sistema CSEB a camada híbrida se mostrou mais fina quando comparada ao sistema SB porém, mais homogênea e compacta ao longo da interface para ambas as situações. Grandes diferenças foram observadas em relação aos tags de resina onde in vivo foram significativamente em menor número, curtos e finos. Para o sistema OUB in vitro a camada híbrida se apresentou fina porém, homogênea em sua extensão com a presença de longos tags. In vivo a camada híbrida se apresentou bastante fina e até difícil de se detectar. O tags se apresentaram quase inexistes ou muito dobrados devido à pobre polimerização desse sistema. As análises em µR para o sistema SB mostraram uma maior contribuição do sistema adesivo nos dois primeiros micrometros da interface, ao passo que, no restante da mesma, houve pouca contribuição dos monômeros adesivos na proteção do colágeno. Para o sistema CSEB a interface se mostrou bastante fina (1µm), para ambas as condições, porém com contribuição, no complexo hibridizado, dos componentes adesivos, colágeno e mineral. Para o sistema OUB in vitro, os espectros também indicaram a presença de uma interface fina, em torno de 1µm, mas também com contribuição dos componentes adesivos, colágeno e mineral. In vivo, esta não pôde ser detectada pelo Raman por ser inexistente ou ser mais fina que a resolução do Raman (1 µm). Realizada as análises da interface em ambas condições experimentais, com os diferentes sistemas adesivos utilizados, conclui-se que: a condição in vivo proporcionou uma interface de menor qualidade para todos os sistemas. O sistema CSEB aparentemente proporcionou uma melhor qualidade de interface e o sistema OUB a pior. O uso dessas três técnicas integradas permitiu uma análise completa, qualitativa e quantitativa da interface adesiva produzida por esses três sistemas, em ambas as condições testadas. / The aim of this research was to analyze in Light Microscopy (LM), micro-Raman Spectroscopy (µR) and Scanning Electron Microscopy (SEM), the dentin-adhesive interface produced by three different bonding systems applied in vivo and in vitro. In in vivo condition patients with the first upper premolars, to be extract for orthodontic reasons, were used. Class I cavities with 0.5mm below the dentin-enamel junction were performed, with carbide bur in high speed. Following, three different bonding systems were applied in accordance with their manufacturer instruction: Single Bond (SB-3M), Clearfil SE Bond (CSEB-KURARAY) and One Up Bond-F (OUBTokuyama), and the cavities restored, incrementally, with composite resin TPH Spectrum (Dentsply). After restoration the teeth were extracted and stored in 0,1% tymol solution. In vitro, the same procedures were performed in extracted upper premolars. Following, the teeth were taken to a cutting machine and cross-sectioned with as diamond saw in specimens with 2mmX2mmx6mm dimensions, being 2 specimens for each tooth. One of the specimen was taken to a hard tissue microtome were 5µm slabs were obtained and stained with Goldner´s Tricrome. The slabs were analyzed in a Light Microscope with 100 times magnification. In this technique, the mineralized dentin is stained green, the collagen is stained red and the bonding system a pale orange. After, the same specimen was used for micro-Raman analysis. The adjacent specimen was dehydrated in ascendant ethanol sequence and analyzed in scanning electron microscopy. The LM results for SB showed the presence of a large area stained red for both conditions, indicating the presence of exposed or non protected collagen by the bonding system. This area was larger in vivo than in vitro. For CSEB this layer war purple stained and consistent along the interface for both situations, indicating, also, collagen available to react with the staining. For OUB this layer was also purple however, in vivo, this layer was thinner and inconsistent than in vitro. In SEM analysis, SB bonding system presented a porous hybrid layer for both situations. In vitro this layer was thicker and regular along the interface and, in vivo, thinner and irregular. Big differences were observed related to the resin tags. In vivo they were thinner and shorter. For CSEB the hybrid layer was thinner when compared with SB however, more homogeneous and compact along the interface for both situations. Big differences were observed related to the resin tags. In vivo, they were significantly in fewer amounts, shorter and thinner. For OUB in vitro, the hybrid layer was thin, however, homogeneous and with long tags. In vivo, the hybrid layer was very thin, almost undetectable. The resin tags were almost non-existent or bended due to poor polymerization of this system. In micro-Raman analysis for SB showed a greater contribution of the bonding system in the first two micrometers of the interface was detected and, in the rest of the interface, there was few contribution of the resin monomers in the collagen protection. For CSEB the interface was thin (1µm), for both conditions, however, with contribution, in the hybridized complex, of the adhesives components, collagen and mineral. For OUB in vitro, the spectras also indicated the presence of a thin interface, among 1µm, but also, with contribution of the bonding components, collagen and mineral. In vivo, the interface could not be detected by the Raman, for being inexistent, or by the fact to be thinner than the Raman resolution (1µm). After all these analysis of the bonding interface, for both conditions, and with these different bonding systems, it can be concluded that: in vivo condition produced a less-quality interface for all the system. CSEB apparently produced a better-quality interface and OUB the worst. The use of these three techniques together allowed a complete analysis, qualitative and quantitative, of the dentin-bonding interface produced by these three bonding systems, for both situations.
| Identifer | oai:union.ndltd.org:IBICT/oai:teses.usp.br:tde-21082009-111925 |
| Date | 17 November 2004 |
| Creators | Fabio Sene |
| Contributors | Jose Carlos Pereira, Carlos de Paula Eduardo, Rosa Helena Miranda Grande, Luis Roberto Marcondes Martins, Paulette Spencer |
| Publisher | Universidade de São Paulo, Odontologia (Dentística), USP, BR |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Biblioteca Digital de Teses e Dissertações da USP, instname:Universidade de São Paulo, instacron:USP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.003 seconds