Previous issue date: 2017-08-18 / Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq) / Transistores de filme fino (TFT) são dispositivos presentes em nosso cotidiano, usados em uma ampla variedade de aplicações, desde de processadores, registradores e monitores de tela plana. Estes dispositivos apresentam diversos benefícios, tais como: transparência, flexibilidade, rapidez, baixo custo e confiabilidade, o que faz com que tenham interesse de muitos grupos de pesquisa nas últimas décadas. Este trabalho visa o desenvolvimento de um novo método de deposição por spray, em atmosfera ambiente e a baixa temperatura (350ºC), para produção de filmes finos de óxidos zinco (ZnO) aplicados como camada ativa em TFTs. Os filmes finos transparentes de ZnO foram depositados por solução de um precursor orgânico (acetato de zinco bi-hidratado (Zn(CH3COO) · 2H2O)) sobre substratos de Si-p/SiO2 pelo método de deposição por spray. Este método emprega uma automação própria de controle na deposição para obter filmes altamente homogêneos e reprodutivos. Um grande conjunto de parâmetros na deposição foram testados para otimização dos filmes semicondutores para TFTs, como por exemplo: distância do spray sobre a placa de aquecimento, tempo de deposição, número de camadas, concentração da solução, entre outros. Os resultados obtidos na caracterização dos dispositivos, como, mobilidade de saturação (µsat), tensão de limiar de operação (Vth) e razão entre a corrente de operação e a corrente intrínseca (ION/OFF), foram comparados para diferentes parâmetros de deposição utilizados. Esse trabalho contribui em utilizar um novo método de deposição de baixo custo, para possíveis aplicações industriais e que pode ser expandido facilmente para larga escala de produção na fabricação de outros dispositivos de filme fino, como, OTFTs (Organic Thin Film Transistors), células solares, LCDs (Liquid Crystal Displays), OLEDs (Organic Light Emitting Diodes), LEDs (Light Emitting Diodes) e sensores. / Thin-film transistors (TFT) are every day devices used in a wide variety of applications, like processors, recorders and flat-panel monitors. These devices that present benefits, such as transparency, flexibility, speed, lower-cost and reliability, which have attracted interest in several research groups in recent decades. The aim of this work is the development of a new method of spray deposition, in ambient atmosphere and at low temperature (350ºC), for the production of thin films of zinc oxide (ZnO) applied as active layer in TFTs. The ZnO thin films were deposited from an organic solution of zinc acetate dihydrate (Zn(CH3COO) · 2H2O) on to Si-p/SiO2 substrates by the spray deposition method. This method employs its own automation for the deposition to obtain highly homogeneous and reproducible films. A large set of parameters in the deposition were tested for optimization of the semiconductor films for TFTs, such as: distance of the spray to the hot-plate, deposition time, number of layers, solution concentration, among others. The results obtained in the characterization of the devices, such as, mobility at saturation (μsat), threshold voltage (Vth) and on/off ratio (ION/OFF), were compared for different deposition parameters. This work contributes to the development of a novel, low-cost deposition method for possible industrial applications that can be easily expanded for large scale production of other thin film devices, such as, Organic Thin Film Transistors (OTFTs), solar cells, LCDs (Liquid Crystal Displays), OLEDs (Organic Light Emitting Diodes), LEDs (Light Emitting Diodes) and sensors. / CNPq: 133952/2015-0
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/151635 |
| Date | 18 August 2017 |
| Creators | Lima, Guilherme Rodrigues de [UNESP] |
| Contributors | Universidade Estadual Paulista (UNESP), Santos, Lucas Fugikawa [UNESP] |
| Publisher | Universidade Estadual Paulista (UNESP) |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | 600 |
Page generated in 0.0029 seconds