In new low-lead and lead-free brass alloys, it is not understood how the corrosion properties,such as dezincification, are related to material composition as well as annealing temperatureand duration. This study aims to fill this knowledge gap by mapping sixteen annealingconditions and three different brass alloy compositions to their respective microstructure anddezincification performance. It was found that high dezincification depth was a result ofannealing temperatures at 300°C – 400°C, which promoted precipitation of intermetallicAlAs-particles along grain boundaries, twins and lead particles as well as precipitation of β-phase along grain boundaries. Their presence was correlated to high micro additions ofaluminium or iron in the material composition. An additional compositional factorcontributing to precipitation of high amount of β-phase was low copper/zinc-ratio.
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-217355 |
| Date | January 2017 |
| Creators | Stålnacke, Emil |
| Publisher | KTH, Materialvetenskap |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0015 seconds