Heat exchanger tubes are commonly made from stainless steel.In a heat exchanger both the process fluid and the cooling orheating media can be corrosive. It is therefore important to beable to select materials that do not suffer from corrosion.Current methods in this area, however, suffer from limitationsand shortcomings. This thesis concerns corrosion tests forgeneral corrosion, dewpoint corrosion and stress corrosioncracking, respectively. For evaluation of general corrosion ofsuperduplex stainless steels in hydrochloric acid and sulphuricacid the importance of activation was studied. The results showthat activation has a great influence on the test result.Further the results indicate that experimental differences canbe the explanation for previously reported differences incorrosion resistance of superduplex stainless steel that havebeen attributed to the alloying with Cu and W. Furthermore, asimple test loop for testing stainless steels under dew formingconditions with a formed condensate of 1 % hydrochloric acidhas been developed. In the work constant strain and constantload test result have been compared and the observationsindicate that the differences can be explained by differencesin the relaxation properties of the materials. <b>Key words:</b>corrosion testing, heat exchanger, stainlesssteel, general corrosion, immersion tests, activation, stresscorrosion cracking, constant load, u-bends, relaxation,dewpoint corrosion / NR 20140805
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-1680 |
| Date | January 2003 |
| Creators | Kivisäkk, Ulf |
| Publisher | KTH, Materialvetenskap, Stockholm : Materialvetenskap |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Licentiate thesis, comprehensive summary, info:eu-repo/semantics/masterThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0016 seconds