Artificial cardiovascular implants are now made mainly from extruded polytetrafluroethylene (PTFE). However, the limited haemocompatibility of PTFE causes blood clotting and results in early replacement. Many techniques are being developed to improve the haemocompatibility of such devices. One of the most promising techniques is to coat the devices with nitrogen-doped diamond-like carbon (NDLC) thin films. However, the structure of NDLC and its effect on the haemocompatibility of the coated devices have not been fully investigated as required for practical applications. In this thesis, ion beam deposited DLC and Nitrogen doped thin films on PTFE were investigated in order to have a better understanding of the relationships between the structure and biomedical properties of the DLC thin films.<p>
DLC and NDLC thin films were synthesized using ion beam deposition. Commercially available PTFE sheets, which are similar to the material used for vascular grafts, were used as substrates for the DLC thin films. Silicon wafers were also utilized as substrates for condition optimization and property comparison. Raman spectroscopy, atomic force microscopy, X-ray photo emission spectroscopy and scanning electron microscopy were used to study the structural and morphological properties of the coated surface. The results show that the ion beam deposited thin films have a very smooth surface and exhibit low coefficient of friction and high adhesion to the substrate. Low concentration of nitrogen doping in DLC improved surface hardness and reduced surface roughness. Higher concentration of sp3 hybridized bonds was observed in the DLC thin films on Si than those on PTFE. DLC coating decreased the surface energy and improved the wettability of PTFE films.<p>
The haemocompatibility of the pristine and DLC coated PTFE sheets were evaluated by platelet adhesion technique. The platelet adhesion results showed that the haemocompatibility of DLC coated PTFE, especially NDLC coated PTFE, was considerably improved as compared with uncoated PTFE. SEM observations showed that the platelet reaction on the coated PTFE was minimized as the platelets were much less aggregated and activated.
Identifer | oai:union.ndltd.org:LACETR/oai:collectionscanada.gc.ca:SSU.etd-08202009-113830 |
Date | 14 September 2009 |
Creators | Sethuraman, Srinivasan |
Contributors | Yang, Qiaoqin |
Publisher | University of Saskatchewan |
Source Sets | Library and Archives Canada ETDs Repository / Centre d'archives des thèses électroniques de Bibliothèque et Archives Canada |
Language | English |
Detected Language | English |
Type | text |
Format | application/pdf |
Source | http://library.usask.ca/theses/available/etd-08202009-113830/ |
Rights | unrestricted, I hereby certify that, if appropriate, I have obtained and attached hereto a written permission statement from the owner(s) of each third party copyrighted matter to be included in my thesis, dissertation, or project report, allowing distribution as specified below. I certify that the version I submitted is the same as that approved by my advisory committee. I hereby grant to University of Saskatchewan or its agents the non-exclusive license to archive and make accessible, under the conditions specified below, my thesis, dissertation, or project report in whole or in part in all forms of media, now or hereafter known. I retain all other ownership rights to the copyright of the thesis, dissertation or project report. I also retain the right to use in future works (such as articles or books) all or part of this thesis, dissertation, or project report. |
Page generated in 0.0018 seconds