Study of the properties of Mg-MgB₂ composites. / 鎂和硼化鎂複合材料的研究 / Study of the properties of Mg-MgB₂ composites. / Mei he peng hua mei fu he cai liao de yan jiu

by Hon Wan Man = 鎂和硼化鎂複合材料的研究 / 韓韻文. / Thesis (M.Phil.)--Chinese University of Hong Kong, 2006. / Includes bibliographical references. / Text in English; abstracts in English and Chinese. / by Hon Wan Man = Mei he peng hua mei fu he cai liao de yan jiu / Han Yunwen. / Abstract --- p.i / 摘要 --- p.iii / Acknowledgements --- p.v / Table of contents --- p.vi / List of tables --- p.x / List of figures --- p.xi / Chapter Chapter 1 --- Introduction --- p.1-1 / Chapter 1.1. --- Background --- p.1-1 / Chapter 1.1.1. --- Conventional and unconventional superconducting materials --- p.1-1 / Chapter 1.1.2. --- Type I and type II superconductors --- p.1-2 / Chapter 1.1.3. --- Critical Temperature and Magnetic Properties (M-H Loops) --- p.1-4 / Chapter 1.2. --- Magnesium Diboride MgB2 --- p.1-6 / Chapter 1.2.1. --- Introduction --- p.1-6 / Chapter 1.2.2. --- Potential application and recent work of MgB2 --- p.1-6 / Chapter 1.2.2.1. --- Thin films --- p.1-7 / Chapter 1.2.2.2. --- Wires and tapes --- p.1-8 / Chapter 1.2.2.3. --- Powders and single crystal --- p.1-8 / Chapter 1.2.3. --- Factors affecting critical temperature in MgB2 --- p.1-9 / Chapter 1.2.3.1. --- Critical temperature versus lattice constants --- p.1-9 / Chapter 1.2.3.2. --- Critical temperature versus pressure --- p.1-9 / Chapter 1.3. --- Mg-based metal matrix composites (Mg-MMCs) --- p.1-10 / Chapter 1.4. --- Objectives and approaches --- p.1-11 / Chapter 1.5. --- Thesis layout --- p.1-12 / Chapter 1.6. --- References --- p.1-13 / Figures --- p.1-16 / Tables --- p.1-20 / Chapter Chapter 2 --- Methodology and instrumentation --- p.2-1 / Chapter 2.1. --- Introduction --- p.2-1 / Chapter 2.2. --- Experimental procedures --- p.2-1 / Chapter 2.3. --- Samples fabrication --- p.2-2 / Chapter 2.3.1. --- Powder metallurgy method (P/M) --- p.2-2 / Chapter 2.3.2. --- Argon atmosphere tube furnace heat treatment --- p.2-3 / Chapter 2.4. --- Characterization --- p.2-3 / Chapter 2.4.1. --- Differential thermal analyzer (DTA) --- p.2-3 / Chapter 2.4.2. --- X-ray powder diffractometry (XRD) --- p.2-4 / Chapter 2.4.3. --- Hot mounting and polishing --- p.2-4 / Chapter 2.4.4. --- Scanning electron microscopy (SEM) --- p.2-5 / Chapter 2.4.5. --- Transmission electron microscopy (TEM) --- p.2-5 / Chapter 2.4.6. --- Vibrating sample magnetometer (VSM) --- p.2-6 / Chapter 2.5. --- References --- p.2-8 / Figures --- p.2-9 / Chapter Chapter 3 --- Effects of sintering temperature on Mg-MgB2 composites --- p.3-1 / Chapter 3.1. --- Introduction --- p.3-1 / Chapter 3.2. --- Experimental results --- p.3-1 / Chapter 3.2.1. --- DTA and XRD analyses --- p.3-1 / Chapter 3.2.2. --- Microstructures --- p.3-2 / Chapter 3.2.2.1. --- Green sample --- p.3-2 / Chapter 3.2.2.2. --- Sample sintered at 550°C --- p.3-3 / Chapter 3.2.2.3. --- Sample sintered at 600°C --- p.3-4 / Chapter 3.2.2.4. --- Sample sintered at 700°C --- p.3-4 / Chapter 3.2.2.5. --- Hexagonal platelets --- p.3-5 / Chapter 3.2.3. --- Superconducting behaviors --- p.3-5 / Chapter 3.2.3.1. --- Critical temperature (Tc) comparison --- p.3-5 / Chapter 3.2.3.2. --- Magnetization loops (M-H loops) --- p.3-6 / Chapter 3.3. --- Discussions --- p.3-7 / Chapter 3.4. --- Conclusions --- p.3-9 / Chapter 3.5. --- References --- p.3-10 / Figures --- p.3-11 / Tables --- p.3-20 / Chapter Chapter 4 --- Effects of composition on Mg-MgB2 composites --- p.4-1 / Chapter 4.1. --- Introduction --- p.4-1 / Chapter 4.2. --- Experimental results --- p.4-1 / Chapter 4.2.1. --- XRD results --- p.4-1 / Chapter 4.2.2. --- Microstructures --- p.4-2 / Chapter 4.2.2.1 --- Mg-0 wt % B (Pure Mg) sintered at 650。C --- p.4-2 / Chapter 4.2.2.2 --- Mg-47 wt % B sintered at 650°C --- p.4-2 / Chapter 4.2.2.3 --- Amount of B in Mg sample --- p.4-3 / Chapter 4.2.2.3.1. --- Overview of Mg-5 to 40 wt % B --- p.4-3 / Chapter 4.2.2.3.2. --- MgB2 phase in different composition (Mg-5 to 47 wt %B) --- p.4-4 / Chapter 4.2.2.3.3. --- MgO phase in different composition (Mg-0 to 30 wt % B) --- p.4-4 / Chapter 4.2.3. --- VSM results (Critical temperature Tc comparison) --- p.4-5 / Chapter 4.3. --- Discussions --- p.4-6 / Chapter 4.4. --- Conclusions --- p.4-8 / Chapter 4.5. --- References --- p.4-10 / Figures --- p.4-11 / Table --- p.4-18 / Chapter Chapter 5 --- Growth Mechanisms --- p.5-1 / Chapter 5.1. --- Introduction --- p.5-1 / Chapter 5.2. --- Brief summary of SEM result --- p.5-1 / Chapter 5.3. --- Growth Mechanism of MgB2 --- p.5-2 / Chapter 5.4. --- Comparison of MgB2 grain size by XRD result --- p.5-7 / Chapter 5.5. --- Stoichiometric Ratio of MgB2 in different temperature --- p.5-7 / Chapter 5.6. --- Growth of the MgB2 platelets --- p.5-8 / Chapter 5.7. --- Conclusions --- p.5-10 / Chapter 5.8. --- References --- p.5-11 / Figures --- p.5-12 / Table --- p.5-15 / Chapter Chapter 6 --- Conclusions and Future Works --- p.6-1 / Chapter 6.1. --- Conclusions --- p.6-1 / Chapter 6.2. --- Future works --- p.6-2 / Chapter 6.3. --- References --- p.6-4

Identiferoai:union.ndltd.org:cuhk.edu.hk/oai:cuhk-dr:cuhk_325771
Date January 2006
ContributorsHon, Wan Man., Chinese University of Hong Kong Graduate School. Division of Materials Science and Engineering.
Source SetsThe Chinese University of Hong Kong
LanguageEnglish, Chinese
Detected LanguageEnglish
TypeText, bibliography
Formatprint, 1 v. (various pagings) : ill. (some col.) ; 30 cm.
RightsUse of this resource is governed by the terms and conditions of the Creative Commons “Attribution-NonCommercial-NoDerivatives 4.0 International” License (http://creativecommons.org/licenses/by-nc-nd/4.0/)

Page generated in 0.0024 seconds