Trapping centres in as-grown TlInS2 layered single crystals have been studied by using a thermally stimulated current (TSC) technique. TSC measurements have been performed in the temperature range of 10-300 K with various heating rates. Experimental evidence has been found for the presence of five trapping centres with activation energies 12, 14, 400, 570 and 650 meV. Their capture cross-sections and concentrations were also determined. It is concluded that in these centres retrapping is negligible as confirmed by the good agreement between the experimental results and the theoretical predictions of the model that assumes slow retrapping. An exponential distribution of traps was revealed from the analysis of the TSC data obtained at different light excitation temperatures.
The transmission and reflection spectra of TlInS2 crystals were measured over the spectral region of 400-1100 nm to determine the absorption coefficient and refractive index. The analysis of the room temperature absorption data revealed the coexistence of the indirect and direct transitions. The absorption edge was observed to shift toward the lower energy values as temperature increases from 10 to 300 K. The oscillator and the dispersion energies, and the zero-frequency refractive index were also reported. Furthermore, the chemical composition of TlInS2 crystals was determined from energy dispersive spectroscopic analysis. The parameters of monoclinic unit cell were found by studying the x-ray powder diffraction.
Identifer | oai:union.ndltd.org:METU/oai:etd.lib.metu.edu.tr:http://etd.lib.metu.edu.tr/upload/12609667/index.pdf |
Date | 01 June 2008 |
Creators | Isik, Mehmet |
Contributors | Bulur, Enver |
Publisher | METU |
Source Sets | Middle East Technical Univ. |
Language | English |
Detected Language | English |
Type | M.S. Thesis |
Format | text/pdf |
Rights | To liberate the content for public access |
Page generated in 0.0013 seconds