The methods HPLC, microcalorimetry and FTIR together with chemometry, provide good analytical tools to follow the degradation of nitro-cellulose. The degradation products formed from diphenylamine (DPA) during storage can be followed with HPLC. FTIR, together with chemometry, also gives the precision needed for safety control of propellants. Nitro-cellulose (NC) containing DPA obtained a green colour already after 1 day storage at 70°C. About 10% of the stabilizer, and its derivatives, added were not extractable giving an extended time to autocatalysis. This time could be extended up to 70 days at 70°C for an extracted sample compared to about 3 days for non-stabilized NC. This was not shown before. Aged and extracted NC samples contained a non-extractable nitro compound. The most likely compound is 2,4´-dinitroDPA, probably bonded to NC via the amine nitrogen. The bonding to NC occurs after the formation of NNODPA. This is something not described before. Using another batch of nitro-cellulose to find out if a chemical bonding occurs gave inconclusive results as a blue NC was formed. Low molecular NC with high stability was obtained. A chemical bonding probably occurs when using NNODPA as a stabilizer, indicating NNODPA plays a key role. The use of FTIR/chemometry is a promising method to use when studying small chemical changes. The described methodology should be used to find out more about the compound(s) being bonded to NC.
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:uu-3989 |
| Date | January 2004 |
| Creators | Lindblom, Torbjörn |
| Publisher | Uppsala universitet, Avdelningen för analytisk kemi, Uppsala : Acta Universitatis Upsaliensis |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Doctoral thesis, comprehensive summary, info:eu-repo/semantics/doctoralThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | Comprehensive Summaries of Uppsala Dissertations from the Faculty of Science and Technology, 1104-232X ; 935 |
Page generated in 0.0082 seconds