Microscopic and spectroscopic studies of growth and electronic structure of epitaxial graphene

It is generally believed that the Si technology is going to hit a road block soon. Amongst all the potential candidates, graphene shows the most promise as replacement material for the aging Si technology. This has caused a tremendous stir in the scientific community. This excitement stems from the fact that graphene exhibits unique electronic properties. Physically, it is a two-dimensional network of spâ‚‚bonded carbon atoms. The unique symmetry of two equivalent sublattices gives rise to a linear energy dispersion for the charge carriers. As a consequence, the charge carriers behave like massless Dirac particles with a constant speed of c/300, where c is the speed of light. The sublattice symmetry gives rise to unique half-integer quantum hall effect, Klein's paradox, and weak antilocalization.

In this research work, I was able to successfully study the growth and electronic structure of EG on SiC(0001), in ultra-high vacuum and low-vacuum furnace environment. I used STM to study the growth at an atomic scale and macroscopic scale. With STM imaging, I studied the distinct properties of commonly observed interface region (layer 0), first graphene layer, and the second graphene layer. I was able to clearly resolve graphene lattice in both layer 1 and 2. High resolution imaging of the defects showed a unique scattering pattern. Raman spectroscopy measurements were done to resolve the layer dependent signatures of EG. The characteristic Raman 2D peak was found to be suppressed in layer 1, and a single Lorentzian was seen in layer 2. Ni metal islands were grown on EG by e-beam deposition. STM/ STS measurements were done to study the changes in doping and the electronic structure of EG with distance from the metal islands.

Identiferoai:union.ndltd.org:GATECH/oai:smartech.gatech.edu:1853/33844
Date06 April 2009
CreatorsSharma, Nikhil
PublisherGeorgia Institute of Technology
Source SetsGeorgia Tech Electronic Thesis and Dissertation Archive
Detected LanguageEnglish
TypeDissertation

Page generated in 0.0018 seconds