The role of sulfur alloying in defects and transitions in copper indium gallium diselenide disulfide thin films

xv, 132 p. : ill. A print copy of this title is available from the UO Libraries, under the call number: SCIENCE TK7871.15.F5 H325 2007 / The effects of sulfur alloying on the electronic properties of CuIn(SeS) 2 and CuInGa(SeS) 2 materials has been investigated using sophisticated junction capacitance techniques including drive-level capacitance profiling and transient photocapacitance and photocurrent spectroscopies. CISSe and CIGSSe materials are used as absorber layers in thin-film photovoltaic devices. By characterizing the electronic properties of these materials we hope to understand how these materials can be improved to make thin-film devices with better conversion efficiencies. Sulfur widens the bandgap of these materials by moving the valence band to lower energies and the conduction band to higher energies. This significantly affects the electronic structure of these devices by increasing the activation energies of dominant acceptor levels and lowering room temperature free hole carrier densities. Using optical spectroscopies we observe a large, broad defect that also changes its apparent energetic depth with sulfur alloying. The occupation of this defect was controlled both optically and thermally, and showed a striking temperature dependence. This temperature dependence was measured by recording the relative defect signal, the ratio of the TPC signal in the defect regime to the above bandgap regime, as a function of temperature. As the temperature of the measurement was decreased, steps in the relative defect signal were observed, indicating the turning off of the thermal pathway that emptied trapped charge from the defect. Remarkably, such steps were seen at the same temperature in CISSe and CIGSSe devices with similar sulfur content. In addition, no steps were seen in CMS devices. This points to a defect state specific to the incorporation of sulfur in the absorber material. We hope that a better understanding of the electronic structure of these materials will assist in the creation of improved wide-bandgap thin-film photovoltaic devices. / Adviser: J. David Cohen

Identiferoai:union.ndltd.org:uoregon.edu/oai:scholarsbank.uoregon.edu:1794/6193
Date12 1900
CreatorsHalverson, Adam Fraser, 1978-
PublisherUniversity of Oregon
Source SetsUniversity of Oregon
Languageen_US
Detected LanguageEnglish
TypeThesis
Format59950 bytes, 4399957 bytes, application/pdf, application/pdf
RelationUniversity of Oregon theses, Dept. of Physics, 2007, Ph. D.