Dissimilar metals joining have been used in many industry fields for various applications due to their technique and beneficial advantages, such as aluminum-steel and magnesium-steel joints for reducing automobile weight, aluminum-copper joint for reducing material cost in electrical components, steel-copper joints for usage in nuclear power plant, etc. The challenges in achieving dissimilar joints are as below. (1) Big difference in physical properties such as melting point and coefficient of thermal expansion led to residual stress and defects. (2) The miscibility issues resulted in either brittle intermetallic compound layer at the welded interface for miscible combinations (such as, aluminum-steel, aluminum-copper, aluminum-titanium, etc.) or no metallurgical bonding for immiscible combinations (such as magnesium-copper, steel-copper, etc.). For metallurgical miscible combinations, brittle intermetallic compounds formed at the welded interface created the crack initiation and propagation path during deformational tests. (3) Stress concentration appeared at the welded interface region during tensile testing due to mismatch in elastic properties of dissimilar materials. In this study, different combinations of dissimilar metals were joined with friction stir welding. Lap welding of 6022-T4 aluminum alloy/galvanized mild steel sheets and 6022-T4 aluminum alloy/DP600 steel sheets were achieved via friction stir scribe technology. The interlocking feature determining the fracture mode and join strength was optimized. Reaction layer (intermetallic compounds layer) between the dissimilar metals were investigated. Butt welding of 5083-H116 aluminum alloy/HSLA-65 steel, 2024-T4 aluminum alloy/316 stainless steel, AZ31/316 stainless steel, WE43/316 stainless steel and 110 copper/316 stainless steel were obtained by friction stir welding. The critical issues in dissimilar metals butt joining were summarized and analyzed in this study including IMC and stress concentration.
| Identifer | oai:union.ndltd.org:unt.edu/info:ark/67531/metadc1404577 |
| Date | 12 1900 |
| Creators | Wang, Tianhao |
| Contributors | Mishra, Rajiv, Reidy, Richard, Du, Jincheng, Scharf, Thomas, Mukherjee, Sundeep |
| Publisher | University of North Texas |
| Source Sets | University of North Texas |
| Language | English |
| Detected Language | English |
| Type | Thesis or Dissertation |
| Format | xviii, 128 pages, Text |
| Rights | Public, Wang, Tianhao, Copyright, Copyright is held by the author, unless otherwise noted. All rights Reserved. |