Nitrogen-doped TiO2 nanotubes with enhanced visible light photocatalytic activity have been synthesized using commercial titania P25 as raw material by a facile P25/urea co-hydrothermal method. Morphological and microstructual characteristics were conducted by transmission electron microscopy, powder X-ray diffraction, and nitrogen adsorption/desorption isotherms; chemical identifications were performed using X-ray photoelectron spectroscopy, and the interstitial nitrogen linkage to the TiO2 nanotubes is identified. The photocatalytic activity of all nitrogen-doped TiO2 nanotubes synthesized by different urea content, evaluated by the decomposition of rhodamine B dye solution under visible light using UV¡VVis absorption spectroscopy, is found to exhibit higher degradation rate than that of P25. Factors affecting the photocatalytic activity of RB were analyzed and a possible mechanism of photodegradation was also proposed. The high photocatalytic activity was attributed to the process of two different mechanisms, one was the direct degradation of the chromophoric system and the other was successive deethylation of the four ethyl groups.
Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0704112-084818 |
Date | 04 July 2012 |
Creators | Lu, Shan-Yu |
Contributors | Li-Heng Kao, Bing-Hwai Hwang, Hung-Yang Lu, Tzu-Chien Hsu |
Publisher | NSYSU |
Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
Language | Cholon |
Detected Language | English |
Type | text |
Format | application/pdf |
Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0704112-084818 |
Rights | user_define, Copyright information available at source archive |
Page generated in 0.0065 seconds