This master‘s thesis deals with study of basic physical, microstructural and mechanical properties of doped piezoceramic materials based on BaTiO3 prepared by electrophoretic deposition. The dopants used were rare earth oxides, i.e. Eu2O3, Er2O3, CeO2, Dy2O3 and Tb4O7 in amounts 1, 3 and 5 wt. %. The influence of dopants and their amount on density, phase composition, mean grain size, hardness, elastic modulus, fracture toughness, and flexural strength was examined. Suitable dopant choice enabled decrease in mean grain size and increase in relative density, hardness, elastic modulus, fracture toughness and flexural strength of sintered specimens. Relative densities up to 99 %, mean grain size below 1 m, hardness up to 13,1 GPa, elastic modulus up to 199 GPa, fracture toughness above 1 MPa·m1/2 and flexural strength above 115 MPa were achieved.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:442597 |
| Date | January 2021 |
| Creators | Zeman, Dominik |
| Contributors | Chlup, Zdeněk, Drdlík, Daniel |
| Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0017 seconds