The object of this study was to investigate the micro-structural response of DP 600 subjected to high strain rate, ballistic impact tests. The ballistic tests were conducted using normal impact of a hardened steel penetrator into a 2 mm thick sheet of DP 600. The average strain rates produced from this test method are on the order of 10^5 s-1. Multiple methods were used to investigate the micro-structure before and after high strain rate deformation including optical microscopy, electron microscopy, and X-ray diffraction. A large variation in material response was observed between tests conducted at 0.8 x 10^5 and 2.5 x 10^5 s-1.