The thesis deals with the study of the influence of concentration and different types of surfactants (Igepal CO-520, Arkopal N110, Igepal CO-890, sodium dodecyl sulfate, sodium dodecylbenzenesulfonate, dodecyltrimethylammonium bromide and Dehyton PL) on the environmental stress cracking resistance of high-density polyethylene by means of Full Notch Creep Test. Furthermore, the influence of ligamental stress (3,5; 4,0 a 4,5 MPa), pH of the prepared active environment and type of the water used as a solvent for the surfactants on the time to failure was monitored. An accelerating effect was observed at increased concentration, stress and molecular weight. Faster failure was achieved after exposure to ionic types compared to nonionic. The rate of the notch opening was determined. The brittle and ductile behavior during the process of failure was evaluated by microscopic analysis of the morphology of the fracture surfaces. Based on the pH change after the test, the stability of the active environment was evaluated. Deteriorating quality of surfactant solutions was observed. Raman spectroscopy and Fourier transform infrared spectroscopy were used to detect the surfactant on the surface of the test specimen after the test.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:444215 |
| Date | January 2021 |
| Creators | Kotoučková, Simona |
| Contributors | Tocháček, Jiří, Bálková, Radka |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0023 seconds