High quality ammonium oxofluorotitanate discoid crystal is successfully grown on glass with an aqueous solution of ammonium hexafluorotitanate and boric acid at the molar ratio of 0.6. The concentration of hydrofluoric acid is less on the glass substrate surface and enhances the ammonium oxofluorotitanate nucleation growth. The growth rate is much higher than that grown on dioctadecyldimethylammonium. From the examinations of X-ray diffraction and high-resolution transmission electron microscopy, the crystal shows high crystalline quality and uniformity. Each titanium oxide octahedral is linked with fluorine and nitrogen atoms. Therefore, ammonium oxofluorotitanate has high potential to be thermally decomposed into high crystalline fluorine and nitrogen co-doped titanium oxide.
A simple process for the preparation of nanocrystalline anatase phase titanium oxide converted from ammonium oxofluorotitanate by thermal treatment was developed. The nanocrystalline anatase phase titanium oxide shows a large bandgap reduction due to the co-doping of high concentrations of fluorine and nitrogen. Due to the excellent nanocrystalline quality and the co-doping of higher concentrations of fluorine and nitrogen at the thermal treatment temperature of 800 OC, it is 1.3 times the photocatalytic activities of P-25 due to the visble region usage of Hg lamp light source. The 11.2 times the visible photocatalytic activities of P-25 using blue light-emitting diode as the light source is obtained from thermal treatment temperature of 600 OC. There is one to one correspondence between carrier lifetime and photocatalytic activity. As a result, a highly reactive and visible-light-driven photocatalysis is achieved.
The heterostructure of zinc selenide/titanium oxide and zinc sulfide/titanium oxide were prepared by metal-organic chemical vapor deposition on the above-prepared titanium oxide. The energy bandgap of zinc sulfide is much larger than that of titanium oxide and can act as a window for titanium oxide. It would not hinder titanium oxide absorption and preserve the role of fluorine and nitrogen co-doping. The energy bandgap of zinc selenide is near the maximum intensity of solar spectrum and acts as a sensitizer of titanium oxide. The lifetime of electron and hole pairs of heterostructure are about 240 and 207 nsec, which are longer than 65 nsec of titanium oxide prepared at 800 oC thermal treatment. Their photocatalytic activities are further improved to 2.0 and 1.5 times higher than that of commercial P-25. The photocatalysis of titanium oxide is very sensitive to the surface states. Titanium oxide surface defects can act as trapping sites for photo-induced holes and facilitate the separation of photo-induced carriers. Zinc selenide and zinc sulfide can passivate the surface well. It may say that titanium oxide surface defects removal has a negative impact.
The density, height, diameter, PL wavelength and intensity of zinc selenide self-assembled quantum dots grown on zinc sulfide/gallium arsenide with the zinc sulfide thickness from 15 to 160 nm are studied. For a fixed 30 sec zinc selenide self-assembled quantum dots growth, it cannot be formed with the zinc sulfide thickness below 15 nm due to the close lattice match between zinc sulfide and gallium arsenide. The zinc sulfide/gallium arsenide is fully lattice relaxed with the zinc sulfide thickness higher than 130 nm examined by X-ray diffraction. The higher quality and density of zinc selenide self-assembled quantum dots can be obtained on zinc sulfide/gallium arsenide with the zinc sulfide thickness far beyond its critical thickness. The maximum zinc selenide self-assembled quantum dots density of 4.9 x 109 cm-2 with the strongest photoluminescence intensity is obtained at the zinc sulfide/gallium arsenide thickness of 130 nm. Clusters are formed on the surface of zinc selenide/gallium arsenide. The selenium segregation is the main mechanism for the formation of clusters. The dislocations will enhance the selenium segregation. Higher zinc selenide cluster corresponds to higher density of dislocations. The non-spherical cluster is formed from the mergence of the two clusters.
High quality zinc oxide rods and zinc hydroxide slices are successfully grown on gallium arsenide with the aqueous solution of zinc nitrate and hexamethylenetetramine. The growth can be controlled by the appropriate nitric acid concentration incorporation in the solution. After thermal annealing, the zinc oxide slices transformed from zinc hydroxide slices can contribute much higher photocatalytic activity to 1.2 times to P-25.
| Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-1222106-232244 |
| Date | 22 December 2006 |
| Creators | Shih, Tsung-Hsiang |
| Contributors | Tsu-Hsin Chang, Chung-Cheng Chang, Jen-Sue Chen, Kuo-Mei Chen, Yu-Hao Yang, Ming-Kwei Lee, Yeong-Her Wang, Jeng Gong |
| Publisher | NSYSU |
| Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
| Language | English |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-1222106-232244 |
| Rights | withheld, Copyright information available at source archive |
Page generated in 0.0016 seconds