This research investigated effect of submicron glass fiber modification on mechanical performance of short carbon fiber reinforced vinyl ester resin. Firstly, the mixture of resin and glass fiber was made by mixing submicron fiber into resin in a homogenizer at the speed of 5000 rpm in 30 minutes. Then, this modified resin was reinforced by short carbon fiber at the length of 1 mm, 3mm and 25 mm. The modifying effects were accessed by evaluating mechanical properties such as: bending, tensile, impact test as well as dynamic mechanical analysis. To explain some manners of material caused by adding glass fiber into resin, some techniques were also used (IFSS, SEM, laser microscope scanner, ultrasonic S-scan, X-ray ...). / 博士(工学) / Doctor of Philosophy in Engineering / 同志社大学 / Doshisha University
| Identifer | oai:union.ndltd.org:doshisha.ac.jp/oai:doshisha.repo.nii.ac.jp:00001611 |
| Date | 22 March 2020 |
| Creators | Nhan Thi Thanh Nguyen |
| Source Sets | Doshisha University |
| Language | English |
| Detected Language | English |
| Type | Thesis or Dissertation |
| Format | application/pdf |
| Source | https://doors.doshisha.ac.jp/opac/opac_link/bibid/BB13142992/?lang=0 |
Page generated in 0.0066 seconds