Indiana University-Purdue University Indianapolis (IUPUI) / The objectives:
1. To compare the flexural strength, flexural modulus, and fracture toughness of specimens fabricated from recently marketed translucent full-contour zirconia, traditional zirconia, and lithium disilicate glass ceramic.
2. To compare the load-to-failure of crowns fabricated from recently marketed translucent full-contour zirconia, traditional zirconia, and lithium disilicate glass ceramic at their recommended tooth-reduction thickness.
Methodology: Four groups of translucent zirconia (BruxZir, KDZ Bruxer, CAP FZ, Suntech zirconia), one group of traditional zirconia (CAP QZ) and IPS e.maxCAD) were tested. Twelve bars of each material were made and tested for flexural strength, and fracture toughness. Fracture patterns were imaged under SEM. Forty-eight crowns (8 from each group) were fabricated with CAD/CAM technique following manufacturers’ recommendations for the amount of tooth reduction. All the crowns were cemented to prepared epoxy resin dies with RelyX Unicem and tested for static load to failure in a universal machine.
Result: In bar-shape samples, CAP QZ (traditional zirconia) showed the highest flexural strength (788.12 MPa), fracture toughness (6.85 MPa.m1/2), and fracture resistance (2489.8 N). All translucent zirconia groups show lower mechanical properties than QZ. However, there were no differences between translucent and traditional zirconia in the fracture resistance of the crown-shape samples. There was no significant difference in fracture resistance between IPS e.max crowns at recommended thickness and other zirconia crowns at recommended thickness.
Conclusion: With less reduction of tooth structure, a high inherent strength and chip resistance make full-zirconia crowns a good alternative to porcelain-fused-to-metal crowns and all other ceramic crowns.
| Identifer | oai:union.ndltd.org:IUPUI/oai:scholarworks.iupui.edu:1805/4015 |
| Date | January 2014 |
| Creators | Janabi, Anmar Uday |
| Contributors | Chu, Tien-Min Gabriel, Matis, Bruce A., Lund, Melvin R., 1922-, Cochran, Michael A. (Michael Alan), 1944-, Cook, Norman Blaine, 1954- |
| Source Sets | Indiana University-Purdue University Indianapolis |
| Language | en_US |
| Detected Language | English |
| Type | Thesis |
Page generated in 0.0019 seconds