In the present work, there was analyzed thermal evolution of the phase transformation in the MgZnAl and MgZnAlCa alloys with different concentration of the Zn and Ca. The grains were occupied by the phase with quasicrystaline icosaedral structure in the as-cast alloys and after isochronal annealing up to 240 řC. The thermal measurements revealed two exothermic effects in the MgZnAl alloy and three exothermic effects in the MgZnAlCa alloy during linear heat treatment in the temperature range of 100 - 250 řC. In agreement to the thermal response, two and three stages of electrical resistivity decrease were observed in the same temperature range. The lower thermal changes, absolute resistivity changes and microhardness were observed in the alloy with Ca-addition and lower concentration of Zn.
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:344176 |
Date | January 2016 |
Creators | Kodetová, Veronika |
Contributors | Vlach, Martin, Mathis, Kristián |
Source Sets | Czech ETDs |
Language | Czech |
Detected Language | English |
Type | info:eu-repo/semantics/masterThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0937 seconds