The electrochemical oxidation and reduction of galena (PbS) was studied in aqueous solutions of perchloric acid between pH 0 and 4. The wide variation of rest potential as reported in the literature was explained on the basis of stoichiometric variations of this material as well as the activities of ionic and molecular species involved in the PbS equilibria. The stoichiometry of the anodic and cathodic reactions was determined to be primarily
PbS ↦ Pb⁺⁺+ S° + 2e⁻
and
PbS + 2H⁺ + 2e⁻↦ Pb° + H₂S
respectively. The irreversibility of anodic oxidation to lead sulphate was observed, with no sulphate produced below about 0.7 to 1.0 volt, depending on the pH. Polarization experiments revealed that ohmic, concentration, and activation polarization effects all contributed to the non-equilibrium behavior of PbS. Reaction of Pb0₂ and MnO₂ with PbS was rapid and interpreted as a "galvanic" effect, relying on the conductivity of the reactants as a necessary condition for its success. / Applied Science, Faculty of / Materials Engineering, Department of / Graduate
Identifer | oai:union.ndltd.org:UBC/oai:circle.library.ubc.ca:2429/35335 |
Date | January 1969 |
Creators | Brodie, John Buchan |
Publisher | University of British Columbia |
Source Sets | University of British Columbia |
Language | English |
Detected Language | English |
Type | Text, Thesis/Dissertation |
Rights | For non-commercial purposes only, such as research, private study and education. Additional conditions apply, see Terms of Use https://open.library.ubc.ca/terms_of_use. |
Page generated in 0.0013 seconds