This dissertation focuses on an electron microscopy investigation of the microstructure of SiC layers in TRISO coated particles deposited by chemical vapour deposition under different experimental conditions, which include temperature, concentration of gases and deposition time. The polycrystalline β-SiC was deposited from the decomposition of methyl trichlorosilane MTS in the presence of hydrogen (H2) as carrier gas. Scanning electron microscopy (SEM), using the backscattered electron (BSE) mode, was used to image the microstructure of and defects in the SiC layers of TRISO particles. Electron backscatter diffraction (EBSD) in the SEM was used to determine the SiC grain sizes and distribution thereof in TRISO particles deposited under different conditions. For samples with a poor EBSD indexing rate, transmission Kikuchi diffraction and transmission electron microscopy (TEM) investigations were also carried out. From the results, the effects of growth temperature on the SiC microstructure, specifically on the grain size and shape and the porosity were determined. The effects of cooling or non-cooling of the gas inlet nozzle on the SiC microstructure were also investigated. TEM and scanning TEM (STEM) analyses of the SiC layers in TRISO particles were performed to image the defects and reveal the crystallinity of SiC layers. The microstructure and composition of SiC tubes fabricated by reaction bonding (RB) was also investigated by using electron microscopy and Raman spectroscopy. SEM-BSE imaging of RBSiC samples allowed the identification of impurities and free silicon in the RBSiC. Finally, the penetration of the metallic fission product, palladium, in reaction bonded SiC at a temperature of a 1000ºC is determined. A brief comment on the suitability of RBSiC as candidate for fuel cladding in a PWR is made. A short discussion of the suitability of the characterisation techniques used is included at the end.
| Identifer | oai:union.ndltd.org:netd.ac.za/oai:union.ndltd.org:nmmu/vital:10553 |
| Date | January 2014 |
| Creators | Ndzane, Nolufefe Muriel |
| Publisher | Nelson Mandela Metropolitan University, Faculty of Science |
| Source Sets | South African National ETD Portal |
| Language | English |
| Detected Language | English |
| Type | Thesis, Masters, MSc |
| Format | xiii, 98 leaves, pdf |
| Rights | Nelson Mandela Metropolitan University |
Page generated in 0.002 seconds