Desenvolvimento e caracterização de nanofibras de acetato de celulose para liberação controlada de fármacos / Development and characterization of cellulose acetate nanofibers for controlled release of drugs

Orientadores: Lucia Helena Innocentini Mei, Marcos Akira dÁvila / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Química / Made available in DSpace on 2018-08-19T17:34:43Z (GMT). No. of bitstreams: 1
Nista_SilviaVazGuerra_M.pdf: 12755531 bytes, checksum: ed049fb5fccf4416e7f0b8a0290222af (MD5)
Previous issue date: 2012 / Resumo: Este projeto foi desenvolvido em duas fases, usando a tecnologia de eletrofiação. A primeira fase foi dedicada a obtenção de membranas eletrofiadas com acetato de celulose, as quais formaram nanofibras que foram carregadas com Sulfato de gentamicina, na segunda fase, para estudos da liberação controlada deste fármaco. Na primeira fase as membranas de nanofibras de Acetato de Celulose, chamadas de nanomembranas, foram produzidas utilizando-se quatro misturas de solventes (Acido Acético/Água (75:25 m/m), Acetona/Água (85:15 m/m), Dimetilacetamida (DMAc)/Acetona (1:2 m/m), Dimetilacetamida/Acetona/Água (32/63/5 m/m)). Usando a ferramenta de planejamento de experimentos (DOE), foram definidos os melhores parâmetros para preparação das membranas nanoestruturadas, em cada sistema de solvente. Três variáveis, sendo a distância entre a agulha e o coletor, a concentração de acetato de celulose na solução e a tensão aplicada, em dois níveis (alto e baixo), foram estudadas em cada sistema. As respostas avaliadas para obtenção da melhor condição, em cada caso, foram o diâmetro médio da fibra obtida e aspecto da membrana formada. Foi realizado também, no sistema de solvente Acido Acético/Água (70:30 m/m), um comparativo entre fiação horizontal, utilizando-se uma taxa de alimentação controlada por uma bomba de infusão, e um sistema vertical onde o fluxo era governado pela gravidade e viscosidade da solução. Um estudo da influencia da taxa de alimentação no diâmetro e aspecto da membrana também foi realizado. Todas as soluções foram avaliadas quanto a sua viscosidade, tensão superficial e condutividade elétrica. Nas soluções de cada sistema de solvente, que apresentaram a melhor condição de processabilidade e melhor membrana, foi realizada uma avaliação do comportamento reológico com a construção de uma curva de Viscosidade versus Taxa de cisalhamento. As melhores membranas obtidas para cada sistema de solvente foram submetidas a um teste de Citotoxicidade para confirmar a biocompatibilidade e sua independência com os resíduos dos solventes utilizados. Na segunda fase utilizaram-se as melhores condições obtidas para cada sistema de solvente e incorporou-se o fármaco Sulfato de Gentamicina em duas concentrações 6 e 60% em massa com base no acetato de celulose. Observou-se a influencia da concentração do fármaco no processo de eletrofiação, no aspecto da membrana formada bem como no diâmetro da nanofibra obtida. A melhor membrana obtida nesta etapa foi produzida a partir do sistema de solventes DMAc/Acetona/Água. As condições de processo utilizadas foram 1 ml/h de vazão, 10 cm de distância entre agulha-coletor e 15 kV de tensão e concentração de acetato de celulose de 15%. Este sistema apresentou-se como um processo bastante viável, não havendo alteração na qualidade da membrana e no processo com a variação da concentração do fármaco. À membrana obtida nestas condições, foi adicionado 50% do fármaco e realizado um teste de liberação com o objetivo de verificar o perfil de liberação do mesmo. Foi realizado um comparativo entre o perfil de liberação desta membrana com o de outras membranas preparadas por casting e com recobrimento de HPMC, Eudragit® L100 e nanofibra eletrofiada de acetato de celulose. O melhor perfil obtido, onde ocorreu uma redução no efeito burst, foi com a membrana revestida com nanofibra, onde foi obtido um ganho de liberação de 9 horas em relação às demais. A melhor membrana obtida também foi submetida a uma análise microbiológica, onde se verificou que o fármaco não perdeu suas propriedades com o processo de eletrofiação / Abstract: This project was developed in two phases, using the technology of electrospinning. The first phase was devoted to obtaining electrospun membranes with cellulose acetate, which formed nanofibers that were loaded with Gentamicin sulphate, in the second phase, for the studies of this drug release. In the first step, these membranes were composed of electrospun nanofibers made of cellulose acetate, here called nanomembranes, using four solvents mixtures (acetic acid/water (75:25 w/w) acetone/water (85:15 w/w), dimethylacetamide(DMAC)/acetone (1:2 w/w), DMAc/acetone/water (32/63/5 w/w). Using the tool for design of experiment (DOE), the best parameters for preparation of nanostructured membranes in each solvent system were fixed. Three variables, such as the distance between the needle and the collector, the concentration of cellulose acetate in solution and the applied voltage, in two levels (high and low), were used in each system. The responses evaluated to obtain the best condition, in each case, were the average diameter of the fiber obtained and the aspect of the membrane formed. In the solvent system formed by acetic acid/water (70:30 w/w), a comparison was carried out between horizontal electrospinning, using an infusion pump to control the feed rate, and a vertical system, whose flow was governed by both gravity and viscosity of the solution. A study of the influence of feed rate on the diameter and aspect of the membranes was done. The viscosity, surface tension and electrical conductivity of all solutions were evaluated. For each system of solvent used, the best parameters of processing ant the best membrane aspect obtained were the chosen for the studies of the rheological behavior of the system by plotting a curve of Viscosity versus Shear rate. The best membranes obtained, for each mixture of solvent used, were submitted to a cytotoxicity test to confirm their biocompatibility and if the residues of any solvent could influence on this test. In the second step of the project, the best conditions obtained for each solvent system were used to electrospun the membranes loaded with gentamicin sulfate in two concentrations, i.e. 6 and 60 wt%, based on cellulose acetate. We observed the influence of the drug concentration in the electrospinning process, as well as the aspect of the membrane formed and the diameters of the nanofibers formed. The best membranes obtained in this step were produced using the solvent system DMAC/acetone/water. The process conditions used were 1 ml/h flow rate, 10 cm distance between needle-collector, 15 kV voltage and 15% cellulose acetate concentration in the solution. This system proved to be a quite feasible process, with no change in the membrane aspect or in the process, for several drug's concentration. To the membrane obtained in these conditions, 50% of the drug was added and the profile of its delivery was observed. A comparison of the releasing profile was also done among this membrane and other membranes prepared by casting and by coating with HPMC, Eudragit ® L100 and electrospun nanofibers of cellulose acetate. The best delivery profile obtained was the membrane coated with nanofiber of acetate solution in DMAC/acetone/water since there was a reduction in the burst effect and a gain in the releasing of 9 hours over the others. The best membrane obtained was also submitted to a microbiological analysis, in which it was verified that the drug did not lose its function during the electrospinning process / Mestrado / Ciencia e Tecnologia de Materiais / Mestre em Engenharia Química

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/266779
Date19 August 2018
CreatorsNista, Silvia Vaz Guerra, 1973-
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, D'Avila, Marcos Akira, 1972-, Mei, Lúcia Helena Innocentini, 1953-, Bretas, Rosario Elida Suman, Martinez, Elizabeth Ferreira
Publisher[s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Química, Programa de Pós-Graduação em Engenharia Química
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Format127 p. : il., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0021 seconds