Submitted by Ivone Costa (mivone@ufpa.br) on 2018-06-25T17:00:41Z
No. of bitstreams: 2
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)
Dissertacao_InfluenciaIncorporacaoLama.pdf.pdf: 3156226 bytes, checksum: f9a5c81200410fe69891ff03a1eca58f (MD5) / Approved for entry into archive by Ivone Costa (mivone@ufpa.br) on 2018-06-25T17:02:48Z (GMT) No. of bitstreams: 2
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)
Dissertacao_InfluenciaIncorporacaoLama.pdf.pdf: 3156226 bytes, checksum: f9a5c81200410fe69891ff03a1eca58f (MD5) / Made available in DSpace on 2018-06-25T17:02:48Z (GMT). No. of bitstreams: 2
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)
Dissertacao_InfluenciaIncorporacaoLama.pdf.pdf: 3156226 bytes, checksum: f9a5c81200410fe69891ff03a1eca58f (MD5)
Previous issue date: 2018-03-29 / A utilização de resíduos na composição mássica argilosa para produção de peças
cerâmicas tem sido amplamente estudada, pois tem-se observado uma melhora
significativa nas propriedades químicas e físicas dos materiais finais. Assim, este
trabalho tem por objetivo avaliar a influência da incorporação de 5 e 10% em peso de
lama de alto forno na massa argilosa, ambas provenientes do estado do Pará. A matériaprima e o resíduo foram inicialmente beneficiados a fim de diminuir o tamanho das
partículas e, posteriormente, passados em peneira com abertura de malha igual a 325
mesh. Após essa etapa, o resíduo e a matéria-prima foram submetido a ensaios de FRX,
EDS, DRX, TG/DTG, distribuição dos tamanhos das partículas, MO, MEV e
determinação do limite de plasticidade e liquidez. Foram preparados corpos de prova
por prensagem uniaxial de 20 Mpa para queima em um forno de laboratório, do tipo
mufla, nas temperaturas de 750, 850 e 950oC. Foram avaliados, MEA, PA, AA, RLQ e
resistência à flexão de três pontos. A microestrutura das cerâmicas queimadas foram
avaliadas por MO, MEV e DRX. Os resultados mostraram que a lama de alto forno é
constituída predominantemente de compostos de ferro, que contribui na colocação
avermelhada na peça sinterizada. O resíduo apresenta uma granulometria favorável a
adição em massa argilosa, não alterando as propriedades tecnológicas. Assim, concluise que a composição com adição de 5% de lama de alto forno foi a que apresentou
resultados favoráveis e exigidos por normas para a fabricação de telhas. / The use of residues in the clay-based ceramic composition for the production of
ceramics has been widely studied, since a significant improvement in the chemical and
physical properties of the final materials has been observed. The aim of this work is to
evaluate the influence of the incorporation of 5 and 10 wt. % of blast furnace sludge
into the clay slag, both from the state of Pará. The raw material and the waste were
initially benefited in order to reduce the particle size and subsequently passed through a
sieve with a mesh opening equal to #325. After this step, the residue and the raw
material were submitted to FRX, EDS, XRD, TG / DTG, particle size distribution, MO,
SEM and determination of plasticity and liquidity limits. Test specimens were prepared
by uniaxial pressing of 20 Mpa for burning in a muffle-type laboratory oven at
temperatures of 750, 850 and 950oC. MEA, PA, AA, RLQ and three-point flexural
strength were evaluated. The microstructure of the burnt ceramics was evaluated by
OM, MEV and XRD. The results showed that the blast furnace slurry consists
predominantly of iron compounds, which contributes to the reddish placement in the
sintered part. The residue presents a granulometry favorable to the addition in clayey
mass, not altering the technological properties. Thus, it was concluded that the
composition with addition of 5% of blast furnace sludge was the one that presented
favorable results and required by standards for the manufacture of tiles.
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpa.br:2011/10059 |
Date | 29 March 2018 |
Creators | COSTA, Roberta Lima de Souza |
Contributors | CANDIDO, Verônica Scarpini |
Publisher | Universidade Federal do Pará, Programa de Pós-Graduação em Engenharia de Processos, UFPA, Brasil, Instituto de Tecnologia |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Source | 1 CD ROM, reponame:Repositório Institucional da UFPA, instname:Universidade Federal do Pará, instacron:UFPA |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0015 seconds