Previous issue date: 2016-06-08 / O presente trabalho trata da obtenção de tinta utilizando dois pigmentos em dois vernizes diferentes (Epóxi–Ep e Poliuretana–PU) e dos testes de eficiência dessas tintas para prevenção da corrosão em aços. Um pigmento a base de Polianilina (Pani) na presença do ácido dodecilbenzeno sulfônico (ADBS) e o outro a base do compósito Pani-Fe3O4. A Pani sintetizada quimicamente foi secada a vácuo e caracterizada pelas técnicas de espectroscopia de Infravermelho e de UV/Vis. As placas de aço carbono SAE 1006 com e sem revestimentos foram submetidas a ensaio cíclico de corrosão em uma câmara de névoa salina (CNS). O monitoramento da corrosão foi feito por análises de fotografia e microscopia óptica. A interação camada-substrato foi investigada por meio da espectroscopia de impedância eletroquímica (EIE) e a superfície dos revestimentos por Espectroscopia Raman. No geral, os resultados indicaram que a Pani-ADBS teve maior desempenho no verniz Ep do que no verniz PU, enquanto o pigmento Pani-Fe3O4 apresentou maior desempenho no verniz PU. Existe evidência de que a Pani-ADBS adicionada ao Ep, na concentração de 0,1%, resulta em melhor proteção do aço ao final do ensaio de 30 dias. O indicativo pode ser visto pela maior resistência (3,95 x 109 ·cm2) e menor capacitância (7,14 x 10-11 F·cm-2). Discussão similar também pode ser feita com o revestimento PU, uma vez que ele apresentou maior resistência da camada (9,81 x 108 ·cm2) e menor capacitância (8,06 x 10-11 F·cm-2). Essa evidência também foi observada pelos resultados de potencial de circuito aberto (Eca). O espalhamento Raman detectou indícios de degradação química dos revestimentos Ep e PU. Baseado nos resultados obtidos neste trabalho é razoável a utilização do modelo ácido-base para explicar o mecanismo de proteção do aço pelos pigmentos Pani-ADBS e Pani-Fe3O4. O mecanismo de proteção do aço ainda carece de mais estudos, entretanto os resultados de potencial de circuito aberto e impedância eletroquímica sugerem que o mecanismo de proteção pode ser explicado por barreira física e em termos de compatibilidade entre o pigmento e a matriz polimérica. / This work describes the production of paints using two pigments in two different polymer matrices (epoxy-Ep and polyurethane-PU) and tests efficiency of these formulations in the prevention of corrosion in steel. A Polyaniline (Pani) based pigment in the presence of a functionalized protonic acid, known as dodecylbenzene sulfonic acid (DBSA) and the other based on Pani-Fe3O4 composite. The chemically synthesized Pani powder was vacuum-dried and characterized by infrared spectroscopy and UV/Vis. The paints were applied to metallic carbon steel SAE 1006 plates. The plates were subjected to cyclic corrosion essay to test the performance of the coatings against corrosion. The film-substrate interaction was investigated by electrochemical impedance spectroscopy (EIS). Raman spectroscopy was used for chemical analysis of surface coatings. It was observed that the Pani-DBSA had its most pronounced effect on the epoxy varnish than in the polyurethane varnish. While the pigment Pani-Fe3O4 showed better performance in the polyurethane varnish. There is evidence that PANI-DBSA added to the Ep at a concentration of 0.1% results in better protection of steel at the end of the 30 day test. This indication can be seen by the increased resistance (3.95 x 109 ·cm2) and a lower capacitance (7.14 x 10-11 F·cm-2). Similar discussion can also be done with the PU coating, as it showed the highest resistance (9.81 x 108 ·cm2) and a lower capacitance (8.06 x 10-11 F·cm-2). These results were confirmed by open circuit the potential (Eoc). The Raman scattering detected chemical evidence of Ep and PU coatings degradation. According to the results obtained in this study, it is reasonable to use the acid-base model to explain the steel protective mechanism by Pani-DBSA and Pani-Fe3O4 pigments. The steel protection mechanism still needs more studies; however, the results of open circuit potential and electrochemical impedance suggest that the protection mechanism can be explained by a physical barrier and in terms of polarity between pigment and matrix.
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpe.br:123456789/18007 |
Date | 08 June 2016 |
Creators | ANDRADE, Gilson Ferreira de |
Contributors | http://lattes.cnpq.br/6705975730240487, DINIZ, Flamarion Borges |
Publisher | Universidade Federal de Pernambuco, Programa de Pos Graduacao em Quimica, UFPE, Brasil |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Source | reponame:Repositório Institucional da UFPE, instname:Universidade Federal de Pernambuco, instacron:UFPE |
Rights | Attribution-NonCommercial-NoDerivs 3.0 Brazil, http://creativecommons.org/licenses/by-nc-nd/3.0/br/, info:eu-repo/semantics/openAccess |
Page generated in 0.0013 seconds