000796599.pdf: 2918256 bytes, checksum: 26733cf0b0b7ecf0a36f4a823e25a1f3 (MD5) / Este trabalho avaliou as propriedades mecânicas e térmicas de materiais compósitos com a base de resina epoxídica curada (DGEBA/TETA) com a adição da ciclodextrina e reforçados com fibras de bagaço de cana-de-açúcar. Primeiramente as fibras foram separadas em tamanhos compreendidos entre 0,50 mm e 2,00 mm, entre 0,21 mm e 0,50 mm e menores que 0,21 mm, as quais foram misturadas à resina DGEBA/TETA e analisadas em porcentagens de 1, 2,5, 5, 7,5 e 10% em massa através de ensaio de tração. Posteriormente, foi adicionado apenas ciclodextrina a resina epóxi em concentrações de 1, 2, 3, 4, 5 e 10 e 15% em massa para a análise de ensaio tração. O corpo de prova final do compósito DGEBA/TETA/ciclodextrina/fibras de bagaço de cana-de-açúcar foi constituído por 5% de ciclodextrina e 5% de partículas menores que 0,21 mm, pois foi o que obteve as melhores propriedades avaliadas em ensaios mecânicos separados. Para a adição de 5% de partículas menores que 0,21 mm ao DGEBA/TETA houve um aumento de 28,61% na resistência, e a adição de 5% de ciclodextrina ao DGEBA/TETA proporcionou um aumento de 160,31% na resistência à propagação de trincas. O compósito final, contendo 5% de partículas de bagaço de cana-de-açúcar e 5% de ciclodextrina apresentou um Limite de Reistência à Tração (LRT) de 33,94 MPa, Módulo de Elasticidade (E) de 1681,14 MPa, K1C de 1,24 MPa.m1/2, resiliência de 0,334 MJ/m3, deformação de 0,292%. Para uma análise da temperatura de uso do compósito, foram realizados ensaios térmicos de DSC e TGA os quais indicaram que a temperatura de Transição vítrea do compósito final foi de 111,18°C e a temperatura de inicio de degradação foi de 267°C / This research evaluated the mechanical and thermal properties of composite materials with the base epoxy resin cured (DGEBA / TETA) with the addition of cyclodextrin and reinforced with fibers of bagasse cane sugar. First the fibers were separated into sizes of between 0.50 mm and 2.00 mm, between 0.21 mm and 0.50 mm and smaller than 0.21 mm, which were mixed resin DGEBA / TETA and analyzed as percentages 1, 2.5, 5, 7.5, 10 and 15% in mass by assaying tensile test. Thereafter was added just cyclodextrin epoxy resin in concentrations of 1, 2, 3, 4, 5 and 10 to 15% in mass to analyze tensile test. The specimen of the composite end DGEBA / TETA / cyclodextrin / bagasse fiber cane sugar that is made up of 5% cyclodextrin and 5% of particles smaller than 0.21 mm that was what got the best properties evaluated in separate mechanical tests. Since for the addition of 5% of particles smaller than 0.21 mm at DGEBA / TETA an increase of 28.61% in the resistance, and the addition of cyclodextrin to 5% DGEBA / TETA provided an increase of 160.31% resistance to crack toughness. The final composite, containing 5% of particles of crushed cane sugar and 5% cyclodextrin showed LRT of 33.94 MPa, E, 1681.14 MPa, K1C of 1.24 MPa.m1/2, resilience 0.334 MJ/m3, deformation of 0.292%. For a review of the use temperature of the composite thermal DSC and TGA tests which indicated that the glass transition temperature of the final composite was 111.18 ° C and the onset temperature of degradation was 267°C were performed
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/111126 |
| Date | 13 March 2014 |
| Creators | Barbosa, Fernando Montanare [UNESP] |
| Contributors | Universidade Estadual Paulista (UNESP), Dias Filho, Newton Luiz [UNESP], Naka, Marco Hiroshi [UNESP] |
| Publisher | Universidade Estadual Paulista (UNESP) |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 134 f. : il. color. |
| Source | Aleph, reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | -1, -1, -1 |
Page generated in 0.0124 seconds