Oxygen strengthened biomedical beta titanium alloys Beta titanium alloy Ti-35Nb-6Ta-7Zr-0.7O (wt. %) exhibits a low Young's modulus and high strength thanks to interstitial strengthening effect of oxygen. These mechanical properties are promising for implant production. In this thesis, the aforementioned alloy is thoroughly studied in conditions prepared by various thermomechanical treatments, namely: material after casting, hot compression testing, die-forging, hot rolling and finally, cold-swaged and annealed condition. Mechanical properties and microstructure of prepared conditions are studied with special interest of enhancing the fatigue performance that is poor after casting due to porosity and large grains. The hot rolling was shown to improve the fatigue performance significantly, mainly through grain refinement. It is shown that by combining the effects of cold-swaging and recrystallization annealing, extensive refinement of grain structure can be achieved. Industrial aspects of implant production by the studied methods were discussed. In the second part of the thesis, the possibility of lowering the Young's modulus by reducing the beta phase stability (by reducing of Nb and Ta content), while retaining high strength caused by high interstitial oxyen content is explored. Several alloys were...
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:380889 |
Date | January 2018 |
Creators | Preisler, Dalibor |
Contributors | Stráský, Josef, Kužel, Radomír |
Source Sets | Czech ETDs |
Language | Czech |
Detected Language | English |
Type | info:eu-repo/semantics/masterThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0015 seconds