INFLUENCE OF TEMPERATURE AND STRESS RATIO ON FATIGUE AND FRACTURE RESPONSE OF HPDC AM60B MAGNESIUM ALLOY

The mechanical behavior of a high pressure die cast AM60B Mg alloy is studied. Constant load amplitude fatigue tests were conducted at room, elevated and cold temperatures, with a stress ratio of R=0.1, and frequency of 30 Hz. The objective was to identify the possible effects of temperature on fatigue life cycle. In addition, fatigue crack propagation tests were conducted to ascertain the fatigue response of the alloy and determine its fatigue crack growth rate as a function of the applied stress ratio, experimentally, analytically and computationally, using Walker’s model. The results demonstrated that temperature had a significant influence on the fatigue life, and that the life increased at cold temperature but decreased at elevated temperature as compared to that evaluated at room temperature. In this study, the limit for applicability of LEFM was established for AM60B magnesium alloy. In addition, fatigue crack propagation test results were used to evaluate the coefficients of the Paris model.

Identiferoai:union.ndltd.org:LACETR/oai:collectionscanada.gc.ca:NSHD.ca#10222/13080
Date19 August 2010
CreatorsHossain, Md. Nur
Source SetsLibrary and Archives Canada ETDs Repository / Centre d'archives des thèses électroniques de Bibliothèque et Archives Canada
LanguageEnglish
Detected LanguageEnglish
TypeThesis

Page generated in 0.0018 seconds