Caracterização dielétrica e eletroóptica do copolímero acrílico funcionalizado com o cromóforo 4-[N-etil-N-(2-hidroxietil)]amino-2-cloro-4-nitro-azobenzeno / Dielectric and electro-optic characterization of the acrylic copolymer containing 4-[N-etyl-N-(2-hydroxietil)]amie-2-cloro-4-nitro-azobenzene group

Neste trabalho foi investigado o processo de relaxação em copolímeros metacrilicos funcionalizados com o grupo cromóforo 4-[N-etil-N-(2-hidroxietil)]amino-2\'-cloro-4\'nitro-azobenzeno (MMADRI3). Os copolímeros sintetizados foram caracterizados por espectrofotometria de visível e infravermelho, calorimetria diferencial de varredura, análise termogravimétrica e elipsometria. O triodo de corona foi utilizado para induzir a orientação dos cromóforos dipolares a temperaturas próximas da transição vítrea. Os valores do coeficiente eletroóptico linear r13 de filmes obtidos por derramento de solução podem alcançar 14 pm/V em amostras funcionalizadas com 43%de cromóforo.O efeito piezoelétricoé significativo para amostras contendo 4% de cromóforo sendo a sua origem atribuída à carga espacial. A relaxação orientacional dos cromóforos foi estudada medindo-se o decaimento do coeficiente eletroóptico e a relaxação dielétrica a diferentes temperaturas. O processo de relaxação foi interpretado utilizando a equação de Kohlraush-Williams-Watts (KWW) aplicada aos domínios do tempo e da freqüência. O tempo de relaxação característico &#964 e o parâmetro b da equação de KWW foram obtidos como função da temperatura desde a temperatura ambiente até acima da temperatura de transição vítrea. O parâmetro b à temperatura de transição vítrea aproxima-se de 0,6 valor que é atribuído a forças de curto alcance. As medidas dielétricas revelaram duas bandas de relaxação &#946 e &#945 respectivamente a baixas e a altas temperaturas. A relaxação a está relacionada com a transição vítrea e à desorientação dos cromóforos. A dependência de &#964 foi fundamentada nas equações de Arrhenius e de Vogel-Fulcher-Tarmnann-Hesse (VFTH), respectivamente a baixas e a altas temperaturas. Os parâmetros de VFTH encontram-se próximos dos considerados universais. O comportamento de &#964 em toda a gama de temperaturas, foi explicado pela equação de Adam-Gibbs, usando-se os parâmetros de VFTH. O resfriamento a taxas lentas após o processo de polarização aumenta substancialmente o tempo de relaxação e a sua energia de ativação. Os expoentes m e n do modelo de Dissado-Hill baseado na interação de multicorpos foram obtidos em função da temperatura. Os valores do parâmetro n ficam dentro do esperado pela teoria / The relaxation process of side-chain methacrylate copolymers functionalized with the nonlinear optical azo chromophore 4-[Nethyl-N-(2-hydroxyethyl)]-amino-2\'-chloro-4-nitroazobenzene (MMADR13) was investigated. The copolymers synthesized were characterized by visible and infrared spectrophotometry, differential scanning calorimetry, thermogravimetric analysis and ellipsometry. The corona triode was employed to induce the orientation of the dipolar chromophore at a temperature near the glass transition. The linear eletrooptic coefficient r13 of cast fllms can reach values as high as 14 pm/V in samples with 43% of chromophore contento The piezoeletric effect attributed to space charge was only significant in the lowest chromophore content samples (4%). Electrostriction was shown to affect to some extent the quadratic electrooptic measurements. The chromophore relaxation at different temperatures was investigated by both electrooptic decay and dielectric measurements. The relaxation process was interpreted using the Kohlraush-Williams-Watts (KWW) equation both in the time and frequency domains. From the KWW equation the characteristic relaxation time &#964 and the stretching parameter b were obtained from room temperature to temperatures above the glass transition. Near the glass transition b is ca 0.6 which is characteristic of short range interactions. Dielectric measurements revealed two relaxation bands, &#946 and &#945, at low and high temperatures, respectively. The &#945 relaxation was attributed to the glass transition and to the 10ss of chromophore orientational order. The temperature behavior of &#964 was interpreted by the Arrhenius and Vogel-Fulcher-Tammann-Hesse (VFTH) equations. at low and high temperatures. respectivelly. The VFTH parameters lie close to the so-called universal values. In addition the overall temperature dependence was explained by the Adam-Gibbs equation using the VFTH parameters. Using a small cooling rate after corona poling increases substantially the relaxation time and the activation energy .The power law exponents m and n. from Dissado-Hill manybody interactions model were obtained as a function of temperature. The n values are in the range of expected values for the many-body interactions model

Identiferoai:union.ndltd.org:usp.br/oai:teses.usp.br:tde-05122014-174109
Date04 October 1999
CreatorsRibeiro, Paulo Antonio Martins Ferreira
ContributorsGiacometti, José Alberto
PublisherBiblioteca Digitais de Teses e Dissertações da USP
Source SetsUniversidade de São Paulo
LanguagePortuguese
Detected LanguageEnglish
TypeTese de Doutorado
Formatapplication/pdf
RightsLiberar o conteúdo para acesso público.

Page generated in 0.0025 seconds